Comprehensive Characterization of B+ Implanted Silicon after Rapid Thermal Annealing

Abstract

Formation of high integrity junctions with low junction leakage and defects is essential for fabricating high performance devices with advanced node devices. Understanding of implant activation and implant damage recovery mechanisms during annealing process steps is limited. Development of noncontact implant activation and residual damage monitoring techniques would be beneficial.