Dual-network hydrogels based on dynamic imine and borate ester bonds with antibacterial and self-healing properties

Abstract

Polymeric hydrogel materials with multiple functions are in great demand in practical biomedical scenarios. In this work, a self-healing hydrogel with both antimicrobial properties was prepared using a strategy that combines dynamic imine and borate ester bonds. In this hydrogel, polyvinyl alcohol (PVA) is used as the base network, and borax solution as the cross-linking agent, and borate ester bonds can be formed between these two. Dialdehyde carboxymethyl cellulose (DCMC) was selected to cross-link with the amino groups in carboxymethyl chitosan (CMCS) and polyethyleneimine (PEI) to form dynamic imine bonds. The PVA/PEI/DCMC/CMCS hydrogels prepared by double chemical cross-linking have good mechanical properties (maximum tensile strength up to 289 KPa and strain at the break up to 1025%). Due to the uniqueness of the two chemical bonds, the hydrogel material is self-healing at room temperature without additional stimulation. In addition, the inherent antibacterial properties of the raw materials in this hydrogel confer antibacterial properties, with a kill rate of up to 99% against E. coli and S. aureus. The multifunctional hydrogels developed in this study provide more ideas and references for the future application of hydrogel materials in practical scenarios.