{"title":"二硅酸锂玻璃陶瓷表面抛光后的形貌、抗弯强度和微观结构分析","authors":"Giordana Picolo Furini, Oscar E Pecho, Pedro Álvarez-Lloret, Paula Benetti","doi":"10.11607/ijp.8352","DOIUrl":null,"url":null,"abstract":"<p><strong>Purpose: </strong>To investigate the influence of finishing, polishing, and glazing on the roughness, flexural strength, and microstructure of lithium disilicate glass-ceramics.</p><p><strong>Materials and methods: </strong>LD CAD/CAM blocks were cut into 96 discs (1.2 × 12 mm). After crystallization, a layer of glaze was applied to the discs' surfaces. The specimens were randomly divided into eight groupsn = 12) for different surface treatments (glaze [G], diamond abrasion [D], find diamond abrasion [F], and polishing [P]): G(glaze, control), GD, GDG, GDP, GF GFG, GFP, and GDFP. Mean roughness (Ra), mean square height (Rq), and maximum roughness (Rz) were measured. The biaxial flexural strength test was performed in a universal testing machine at 0.5 mm/minute. Microstructural analysis was performed using x-ray diffraction patterns (XRD). Differences on the roughness obtained in distinct groups was analyzed with Kruskal-Wallis and Bonferroni tests (α = .05). The flexural strength tests were compared with one-way ANOVA.</p><p><strong>Results: </strong>Glazed groups (G, GDG, and GFG) presented the lowest surface roughness, lower crystallinity, and higher flexural strength than the other groups. Although polishing and glaze presented similar surface roughness, polishing protocol decreased the flexural strength compared to the control group G.</p><p><strong>Conclusions: </strong>Clinically adjusted LD glass-ceramic restorations should be reglazed whenever possible to improve strength.</p>","PeriodicalId":50292,"journal":{"name":"International Journal of Prosthodontics","volume":" ","pages":"439-446"},"PeriodicalIF":2.1000,"publicationDate":"2024-08-23","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Analysis of Topography, Flexural Strength, and Microstructure of a Lithium Disilicate Glass- Ceramic after Surface Finishing.\",\"authors\":\"Giordana Picolo Furini, Oscar E Pecho, Pedro Álvarez-Lloret, Paula Benetti\",\"doi\":\"10.11607/ijp.8352\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p><strong>Purpose: </strong>To investigate the influence of finishing, polishing, and glazing on the roughness, flexural strength, and microstructure of lithium disilicate glass-ceramics.</p><p><strong>Materials and methods: </strong>LD CAD/CAM blocks were cut into 96 discs (1.2 × 12 mm). After crystallization, a layer of glaze was applied to the discs' surfaces. The specimens were randomly divided into eight groupsn = 12) for different surface treatments (glaze [G], diamond abrasion [D], find diamond abrasion [F], and polishing [P]): G(glaze, control), GD, GDG, GDP, GF GFG, GFP, and GDFP. Mean roughness (Ra), mean square height (Rq), and maximum roughness (Rz) were measured. The biaxial flexural strength test was performed in a universal testing machine at 0.5 mm/minute. Microstructural analysis was performed using x-ray diffraction patterns (XRD). Differences on the roughness obtained in distinct groups was analyzed with Kruskal-Wallis and Bonferroni tests (α = .05). The flexural strength tests were compared with one-way ANOVA.</p><p><strong>Results: </strong>Glazed groups (G, GDG, and GFG) presented the lowest surface roughness, lower crystallinity, and higher flexural strength than the other groups. Although polishing and glaze presented similar surface roughness, polishing protocol decreased the flexural strength compared to the control group G.</p><p><strong>Conclusions: </strong>Clinically adjusted LD glass-ceramic restorations should be reglazed whenever possible to improve strength.</p>\",\"PeriodicalId\":50292,\"journal\":{\"name\":\"International Journal of Prosthodontics\",\"volume\":\" \",\"pages\":\"439-446\"},\"PeriodicalIF\":2.1000,\"publicationDate\":\"2024-08-23\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"International Journal of Prosthodontics\",\"FirstCategoryId\":\"3\",\"ListUrlMain\":\"https://doi.org/10.11607/ijp.8352\",\"RegionNum\":4,\"RegionCategory\":\"医学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"DENTISTRY, ORAL SURGERY & MEDICINE\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"International Journal of Prosthodontics","FirstCategoryId":"3","ListUrlMain":"https://doi.org/10.11607/ijp.8352","RegionNum":4,"RegionCategory":"医学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"DENTISTRY, ORAL SURGERY & MEDICINE","Score":null,"Total":0}
Analysis of Topography, Flexural Strength, and Microstructure of a Lithium Disilicate Glass- Ceramic after Surface Finishing.
Purpose: To investigate the influence of finishing, polishing, and glazing on the roughness, flexural strength, and microstructure of lithium disilicate glass-ceramics.
Materials and methods: LD CAD/CAM blocks were cut into 96 discs (1.2 × 12 mm). After crystallization, a layer of glaze was applied to the discs' surfaces. The specimens were randomly divided into eight groupsn = 12) for different surface treatments (glaze [G], diamond abrasion [D], find diamond abrasion [F], and polishing [P]): G(glaze, control), GD, GDG, GDP, GF GFG, GFP, and GDFP. Mean roughness (Ra), mean square height (Rq), and maximum roughness (Rz) were measured. The biaxial flexural strength test was performed in a universal testing machine at 0.5 mm/minute. Microstructural analysis was performed using x-ray diffraction patterns (XRD). Differences on the roughness obtained in distinct groups was analyzed with Kruskal-Wallis and Bonferroni tests (α = .05). The flexural strength tests were compared with one-way ANOVA.
Results: Glazed groups (G, GDG, and GFG) presented the lowest surface roughness, lower crystallinity, and higher flexural strength than the other groups. Although polishing and glaze presented similar surface roughness, polishing protocol decreased the flexural strength compared to the control group G.
Conclusions: Clinically adjusted LD glass-ceramic restorations should be reglazed whenever possible to improve strength.
期刊介绍：
Official Journal of the European Association for Osseointegration (EAO), the International College of Prosthodontists (ICP), the German Society of Prosthodontics and Dental Materials Science (DGPro), and the Italian Academy of Prosthetic Dentistry (AIOP)
Prosthodontics demands a clinical research emphasis on patient- and dentist-mediated concerns in the management of oral rehabilitation needs. It is about making and implementing the best clinical decisions to enhance patients'' quality of life via applied biologic architecture - a role that far exceeds that of traditional prosthetic dentistry, with its emphasis on materials and techniques. The International Journal of Prosthodontics is dedicated to exploring and developing this conceptual shift in the role of today''s prosthodontist, clinician, and educator alike. The editorial board is composed of a distinguished team of leading international scholars.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号