低温烧成钇铁石榴石厚膜的印刷性能及结构分析

2015 IEEE Regional Symposium on Micro and Nanoelectronics (RSM) Pub Date : 2015-08-01 DOI:10.1109/RSM.2015.7355017

I. H. Hasan, M. Hamidon, I. Ismail, R. Osman, S. Azhari

{"title":"低温烧成钇铁石榴石厚膜的印刷性能及结构分析","authors":"I. H. Hasan, M. Hamidon, I. Ismail, R. Osman, S. Azhari","doi":"10.1109/RSM.2015.7355017","DOIUrl":null,"url":null,"abstract":"This paper presents results of study on Yttrium iron garnet (YIG) thick film paste using linseed oil as organic binder. YIG nanopowder is mixed with organic vehicle which consists of linseed oil, m-xylene and α-terpineol. Samples with different ratios of compositions are prepared to study the printability and adhesion properties of the paste. Paste samples were then screen printed onto alumina substrate, dried and fired at 300°C. Microscopic images of the samples were observed to determine most suitable ratio for producing YIG paste. Based on the results, YIG paste with 30 wt% ratio showed good adhesion to the substrate as well as having high dielectric property compared to pastes with lower powder ratio.","PeriodicalId":6667,"journal":{"name":"2015 IEEE Regional Symposium on Micro and Nanoelectronics (RSM)","volume":"14 1","pages":"1-4"},"PeriodicalIF":0.0000,"publicationDate":"2015-08-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"3","resultStr":"{\"title\":\"Printability and structural analysis of Yttrium iron garnet thick film with low firing temperature\",\"authors\":\"I. H. Hasan, M. Hamidon, I. Ismail, R. Osman, S. Azhari\",\"doi\":\"10.1109/RSM.2015.7355017\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"This paper presents results of study on Yttrium iron garnet (YIG) thick film paste using linseed oil as organic binder. YIG nanopowder is mixed with organic vehicle which consists of linseed oil, m-xylene and α-terpineol. Samples with different ratios of compositions are prepared to study the printability and adhesion properties of the paste. Paste samples were then screen printed onto alumina substrate, dried and fired at 300°C. Microscopic images of the samples were observed to determine most suitable ratio for producing YIG paste. Based on the results, YIG paste with 30 wt% ratio showed good adhesion to the substrate as well as having high dielectric property compared to pastes with lower powder ratio.\",\"PeriodicalId\":6667,\"journal\":{\"name\":\"2015 IEEE Regional Symposium on Micro and Nanoelectronics (RSM)\",\"volume\":\"14 1\",\"pages\":\"1-4\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2015-08-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"3\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"2015 IEEE Regional Symposium on Micro and Nanoelectronics (RSM)\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1109/RSM.2015.7355017\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"2015 IEEE Regional Symposium on Micro and Nanoelectronics (RSM)","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1109/RSM.2015.7355017","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}

引用次数: 3

摘要

本文介绍了以亚麻油为有机结合剂制备钇铁石榴石(YIG)厚膜浆料的研究结果。YIG纳米粉体与亚麻籽油、间二甲苯和α-松油醇组成的有机载体混合。制备了不同配比的样品，研究了浆料的印刷性能和粘附性能。然后将膏体样品丝网印刷到氧化铝基板上，干燥并在300°C下烧制。观察样品的显微图像，以确定生产YIG膏体的最合适比例。结果表明，与低粉比的YIG浆料相比，质量比为30 %的YIG浆料与基体的粘附性好，具有较高的介电性能。

本文章由计算机程序翻译，如有差异，请以英文原文为准。

查看原文本刊更多论文

Printability and structural analysis of Yttrium iron garnet thick film with low firing temperature

This paper presents results of study on Yttrium iron garnet (YIG) thick film paste using linseed oil as organic binder. YIG nanopowder is mixed with organic vehicle which consists of linseed oil, m-xylene and α-terpineol. Samples with different ratios of compositions are prepared to study the printability and adhesion properties of the paste. Paste samples were then screen printed onto alumina substrate, dried and fired at 300°C. Microscopic images of the samples were observed to determine most suitable ratio for producing YIG paste. Based on the results, YIG paste with 30 wt% ratio showed good adhesion to the substrate as well as having high dielectric property compared to pastes with lower powder ratio.