Study of the surface properties of ultrathin films of poly(dimethylsiloxane)‐polyamide multiblock copolymers

Ultrathin films of poly(dimethylsiloxane)-polyamide copolymers (PAS) with different silicone contents were prepared by the methods of water casting and spin coating. The surface properties of the films were investigated in detail using contact angle measurements and X-ray photoelectron spectroscopy (XPS). The water-cast films were thin enough to be applicable as laminate films for an artificial lung or an air-separator for oxygen-enrichted air. Uniform and ultrathin films were obtained by the spin coating method. XPS and contact angle measurements suggested that poly(dimethylsiloxane) segments were condensed at the outermost surface of spin-coated PAS films. XPS measurements also revealed that the surface properties of PAS were affected by the molding method, especially the solvent evaporation conditions. Ultradunne Filme aus Polydimethylsiloxan(PDMS)-Polyamid-Copolymeren (PAS) mit unterschiedlichen Silikonanteilen wurden durch Filmgiesen auf Wasser und Rotationsbeschichten hergestellt. Die Oberflacheneigenschaften der Filme wurden mittels Kontaktwinkelmessungen und Rontgenphotoelektronenspektroskopie (XPS) untersucht. Die auf Wasser gegossenen Filme waren dunn genug, um als Laminatfilme in kunstlichen Lungen oder als Trennmembranen zur Sauerstoffanreicherung von Luft Anwendung finden zu konnen. Gleichmasig dicke und ultradunne Filme wurden durch Rotationsbeschichten erhalten. Aus den XPS- und Kontaktwinkelmessungen kann geschlossen werden, das sich die PDMS-Segmente an der Oberflache der Filme anreichern. Aus den XPS-Messungen geht auserdem hervor, das die Oberflacheneigenschaften von PAS von der Herstellungsmethode, insbesondere von den Bedingungen der Losemittelverdampfung abhangen.