同时脱碳氮化Hi-B钢再结晶退火后组织和织构的表征

IF 3.1 2区 材料科学 Q1 METALLURGY & METALLURGICAL ENGINEERING
Li Xiang , Zhe Rong , Bing Fa , Hai-jun Wang , Sheng-tao Qiu
{"title":"同时脱碳氮化Hi-B钢再结晶退火后组织和织构的表征","authors":"Li Xiang ,&nbsp;Zhe Rong ,&nbsp;Bing Fa ,&nbsp;Hai-jun Wang ,&nbsp;Sheng-tao Qiu","doi":"10.1016/S1006-706X(18)30020-7","DOIUrl":null,"url":null,"abstract":"<div><p>How to manufacture the high magnetic induction grain-oriented silicon steel (Hi-B steel) by the process featured with the primary recrystallization annealing was demonstrated, during which nitriding and decarburizing were simultaneously realized in laboratory. By the techniques of optical microscope, scanning electronic microscope and electron backscattered diffraction, both the microstructure and the texture in the samples were characterized. The samples had been subjected to nitriding to different nitrogen contents at two specified temperatures using the two defined microstructural parameters : the grain size inhomogeneity factor σ* and the texture factor AR. The former is the ratio of the mean value to standard deviation of grain sizes; the latter is the ratio of the total volume fraction of the harmful textures to that of beneficial textures including {110} &lt;001&gt;. When the N content increased from 0. 0055 <em>%</em> to 0. 0330% after the annealing at both 835 and 875 °C, the resultant recrystallized grain size decreased hut <em>σ</em>* changed little; whilst the rise of annealing temperature from 835 to 875 °C resulted in the increase in both grain size and σ*. Moreover, either the injected N content or temperature had insignificant influence on the components of primary recrystallization texture developed during annealing. However, the increase of temperature led to the decreases in both intensity and volume fraction of {001} &lt;120&gt; and {110} &lt;001&gt; textures but increases in the {114} &lt;481&gt; and γ fiber textures and the resultant decrease of AR.</p></div>","PeriodicalId":64470,"journal":{"name":"Journal of Iron and Steel Research(International)","volume":null,"pages":null},"PeriodicalIF":3.1000,"publicationDate":"2017-12-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://sci-hub-pdf.com/10.1016/S1006-706X(18)30020-7","citationCount":"4","resultStr":"{\"title\":\"Characterizing microstructure and texture after recrystallization annealing of Hi-B steel with simutaneous decarburization and nitriding\",\"authors\":\"Li Xiang ,&nbsp;Zhe Rong ,&nbsp;Bing Fa ,&nbsp;Hai-jun Wang ,&nbsp;Sheng-tao Qiu\",\"doi\":\"10.1016/S1006-706X(18)30020-7\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><p>How to manufacture the high magnetic induction grain-oriented silicon steel (Hi-B steel) by the process featured with the primary recrystallization annealing was demonstrated, during which nitriding and decarburizing were simultaneously realized in laboratory. By the techniques of optical microscope, scanning electronic microscope and electron backscattered diffraction, both the microstructure and the texture in the samples were characterized. The samples had been subjected to nitriding to different nitrogen contents at two specified temperatures using the two defined microstructural parameters : the grain size inhomogeneity factor σ* and the texture factor AR. The former is the ratio of the mean value to standard deviation of grain sizes; the latter is the ratio of the total volume fraction of the harmful textures to that of beneficial textures including {110} &lt;001&gt;. When the N content increased from 0. 0055 <em>%</em> to 0. 0330% after the annealing at both 835 and 875 °C, the resultant recrystallized grain size decreased hut <em>σ</em>* changed little; whilst the rise of annealing temperature from 835 to 875 °C resulted in the increase in both grain size and σ*. Moreover, either the injected N content or temperature had insignificant influence on the components of primary recrystallization texture developed during annealing. However, the increase of temperature led to the decreases in both intensity and volume fraction of {001} &lt;120&gt; and {110} &lt;001&gt; textures but increases in the {114} &lt;481&gt; and γ fiber textures and the resultant decrease of AR.</p></div>\",\"PeriodicalId\":64470,\"journal\":{\"name\":\"Journal of Iron and Steel Research(International)\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":3.1000,\"publicationDate\":\"2017-12-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://sci-hub-pdf.com/10.1016/S1006-706X(18)30020-7\",\"citationCount\":\"4\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Journal of Iron and Steel Research(International)\",\"FirstCategoryId\":\"1087\",\"ListUrlMain\":\"https://www.sciencedirect.com/science/article/pii/S1006706X18300207\",\"RegionNum\":2,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q1\",\"JCRName\":\"METALLURGY & METALLURGICAL ENGINEERING\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Iron and Steel Research(International)","FirstCategoryId":"1087","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S1006706X18300207","RegionNum":2,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"METALLURGY & METALLURGICAL ENGINEERING","Score":null,"Total":0}
引用次数: 4

摘要

介绍了利用一次再结晶退火工艺制备高磁感应度晶粒取向硅钢(Hi-B钢)的工艺过程,并在实验室中同时实现了渗氮和脱碳。利用光学显微镜、扫描电镜和电子背散射衍射技术对样品的微观结构和织构进行了表征。利用确定的晶粒尺寸不均匀系数σ*和织构系数AR(晶粒尺寸均值与标准差之比)这两个微观组织参数,在两个特定温度下对样品进行不同氮含量的渗氮处理;后者为有害织构与包括{110}<001>在内的有益织构的总体积分数之比。当N含量从0。0055 %至0。在835℃和875℃退火后,得到的再结晶晶粒尺寸减小,但σ*变化不大;退火温度从835℃升高到875℃,晶粒尺寸增大,σ*增大。此外,注入氮含量和温度对退火过程中形成的初级再结晶织构的组成影响不显著。然而,温度升高导致{001}<120>{110} <001>纹理,但{114}<481>和γ纤维织构以及由此导致的AR降低。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
Characterizing microstructure and texture after recrystallization annealing of Hi-B steel with simutaneous decarburization and nitriding

How to manufacture the high magnetic induction grain-oriented silicon steel (Hi-B steel) by the process featured with the primary recrystallization annealing was demonstrated, during which nitriding and decarburizing were simultaneously realized in laboratory. By the techniques of optical microscope, scanning electronic microscope and electron backscattered diffraction, both the microstructure and the texture in the samples were characterized. The samples had been subjected to nitriding to different nitrogen contents at two specified temperatures using the two defined microstructural parameters : the grain size inhomogeneity factor σ* and the texture factor AR. The former is the ratio of the mean value to standard deviation of grain sizes; the latter is the ratio of the total volume fraction of the harmful textures to that of beneficial textures including {110} <001>. When the N content increased from 0. 0055 % to 0. 0330% after the annealing at both 835 and 875 °C, the resultant recrystallized grain size decreased hut σ* changed little; whilst the rise of annealing temperature from 835 to 875 °C resulted in the increase in both grain size and σ*. Moreover, either the injected N content or temperature had insignificant influence on the components of primary recrystallization texture developed during annealing. However, the increase of temperature led to the decreases in both intensity and volume fraction of {001} <120> and {110} <001> textures but increases in the {114} <481> and γ fiber textures and the resultant decrease of AR.

求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
CiteScore
4.30
自引率
0.00%
发文量
2879
审稿时长
3.0 months
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
确定
请完成安全验证×
copy
已复制链接
快去分享给好友吧!
我知道了
右上角分享
点击右上角分享
0
联系我们:info@booksci.cn Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。 Copyright © 2023 布克学术 All rights reserved.
京ICP备2023020795号-1
ghs 京公网安备 11010802042870号
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术官方微信