Amorphization, Crystallization, and Magnetic Properties of Melt-Spun Alloys

Effects of Cr3C2 content and wheel surface speed on the amorphous formation ability and magnetic properties have been investigated for melt-spun () alloys. Ribbon melt-spun at lower wheel speed (30 m/s) has composite structure composed of mostly SmCo7, a small amount of Sm2Co17, and residual amorphous phases. The grain size of SmCo7 phase decreases with the increase of Cr3C2 content . When melt spinning at 40 m/s, alloys can be obtained in the amorphous state for with intrinsic coercive of the order of 40–70 Oe. DSC analysis reveals that SmCo7 phase first precipitates from the amorphous matrix at 650∘C, followed by the crystallization of Sm2Co17 phase at 770∘C. Optimal coercivity of 7.98 kOe and remanent magnetization of 55.05 emu/g have been realized in magnet subjected to melt spinning at 40 m/s and annealing at 650∘C for 5 min. The domain structure of the annealed ribbon is composed of interaction domains typically 100–400 nm in size, which indicates the presence of a strong exchange coupling between the grains.