E. Ching-Prado, W. Pérez, R. Katiyar, A. Garg, D. C. Agrawal
{"title":"Pb(Zr,Ti,Ce)O/sub - 3/陶瓷的结构和热研究","authors":"E. Ching-Prado, W. Pérez, R. Katiyar, A. Garg, D. C. Agrawal","doi":"10.1109/ISAF.1994.522310","DOIUrl":null,"url":null,"abstract":"Solid solution having compositions Pb[Zr/sub x-y/Ce/sub y/Ti/sub 1-x/]O/sub 3/ with y=0.0, 0.001, 0.00125, and 0.02 were studied. The samples were prepared from sintered oxides. XRD measurements indicate a mixture of rhombohedral and tetragonal phases in all the samples, where the tetragonal phase increases with increasing CeO/sub 2/ concentration. Also, the c/a ratio of the tetragonal structure was found to increase with increasing CeO/sub 2/, content. Precipitation of cerium oxide was observed for the sample with y=0.02, showing that the solubility of CeO/sub 2/ in lead zirconate is lower than 2%. Raman scattering measurements confirm that all the samples are perovskite in structure, but inhomogeneities were found. The strong line around 465 cm/sup -1/, corresponding to F/sub 2g/ symmetry, shows the presence of cerium oxide in the sample with y=0.02. Finally, DSC measurements show that the Curie temperature decreases with increasing CeO/sub 2/ content.","PeriodicalId":20488,"journal":{"name":"Proceedings of 1994 IEEE International Symposium on Applications of Ferroelectrics","volume":"28 1","pages":"108-110"},"PeriodicalIF":0.0000,"publicationDate":"1994-08-07","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Structural and thermal study of Pb(Zr,Ti,Ce)O/sub 3/ ceramics\",\"authors\":\"E. Ching-Prado, W. Pérez, R. Katiyar, A. Garg, D. C. Agrawal\",\"doi\":\"10.1109/ISAF.1994.522310\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Solid solution having compositions Pb[Zr/sub x-y/Ce/sub y/Ti/sub 1-x/]O/sub 3/ with y=0.0, 0.001, 0.00125, and 0.02 were studied. The samples were prepared from sintered oxides. XRD measurements indicate a mixture of rhombohedral and tetragonal phases in all the samples, where the tetragonal phase increases with increasing CeO/sub 2/ concentration. Also, the c/a ratio of the tetragonal structure was found to increase with increasing CeO/sub 2/, content. Precipitation of cerium oxide was observed for the sample with y=0.02, showing that the solubility of CeO/sub 2/ in lead zirconate is lower than 2%. Raman scattering measurements confirm that all the samples are perovskite in structure, but inhomogeneities were found. The strong line around 465 cm/sup -1/, corresponding to F/sub 2g/ symmetry, shows the presence of cerium oxide in the sample with y=0.02. Finally, DSC measurements show that the Curie temperature decreases with increasing CeO/sub 2/ content.\",\"PeriodicalId\":20488,\"journal\":{\"name\":\"Proceedings of 1994 IEEE International Symposium on Applications of Ferroelectrics\",\"volume\":\"28 1\",\"pages\":\"108-110\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"1994-08-07\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Proceedings of 1994 IEEE International Symposium on Applications of Ferroelectrics\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1109/ISAF.1994.522310\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Proceedings of 1994 IEEE International Symposium on Applications of Ferroelectrics","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1109/ISAF.1994.522310","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Structural and thermal study of Pb(Zr,Ti,Ce)O/sub 3/ ceramics
Solid solution having compositions Pb[Zr/sub x-y/Ce/sub y/Ti/sub 1-x/]O/sub 3/ with y=0.0, 0.001, 0.00125, and 0.02 were studied. The samples were prepared from sintered oxides. XRD measurements indicate a mixture of rhombohedral and tetragonal phases in all the samples, where the tetragonal phase increases with increasing CeO/sub 2/ concentration. Also, the c/a ratio of the tetragonal structure was found to increase with increasing CeO/sub 2/, content. Precipitation of cerium oxide was observed for the sample with y=0.02, showing that the solubility of CeO/sub 2/ in lead zirconate is lower than 2%. Raman scattering measurements confirm that all the samples are perovskite in structure, but inhomogeneities were found. The strong line around 465 cm/sup -1/, corresponding to F/sub 2g/ symmetry, shows the presence of cerium oxide in the sample with y=0.02. Finally, DSC measurements show that the Curie temperature decreases with increasing CeO/sub 2/ content.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号