Biomolecules Electrochemical Sensing Properties of a PMo11V@N-Doped Few Layer Graphene Nanocomposite

A novel hybrid nanocomposite, PMo11V@N-doped few layer graphene, was prepared by a one-step protocol through direct immobilization of the tetrabutylammonium salt of a vanadium-substituted phosphomolybdate (PMo11V) onto N-doped few layer graphene (N-FLG). The nanocomposite characterization by FTIR and XPS confirmed its successful synthesis. Glassy carbon modified electrodes with PMo11V and PMo11V@N-FLG showed cyclic voltammograms consistent with surface-confined redox processes attributed to Mo-centred reductions (MoVI→MoV) and a vanadium reduction (VV→VIV). Furthermore, PMo11V@N-FLG modified electrodes showed good stability and well-resolved redox peaks with high current intensities. The observed enhancement of PMo11V electrochemical properties is a consequence of a strong electronic communication between the POM and the N-doped few layer graphene. Additionally, the electro-catalytic and sensing properties towards acetaminophen (AC) and theophylline (TP) were evaluated by voltammetric techniques using a glassy carbon electrode modified with PMo11V@N-FLG. Under the conditions used, the square wave voltammetric peak current increased linearly with AC concentration in the presence of TP, but showing two linear ranges: 1.2 × 10−6 to 1.2 × 10−4 and 1.2 × 10−4 to 4.8 × 10−4 mol dm−3, with different AC sensitivity values, 0.022 A/mol dm−3 and 0.035 A/mol dm−3, respectively (detection limit, DL = 7.5 × 10−7 mol dm−3).