Mechanical Properties and Chemical Stability of Bathroom Wall Composites Manufactured from Recycled Polyethylene Terephthalate (PET) Mixed with Cocoa Hulls Powder

The need to protect our environment by eliminating plastic waste as much as possible and by recycling waste from agricultural residue, has led us to formulate composites based on polyethylene terephthalate (PET) loaded with powder from the cocoa shell. The cocoa hulls were prior treated with organosolv process to improve the fiber-matrix interaction. This research is aimed at manufacturing composite wall tiles from recycled PET reinforced with cocoa hull powder (CCP). The composites were manufactured by the melt-mixing method followed by compression molding. The mechanical, physico-chemical properties and the stability to environmental conditions were evaluated. The results showed that the incorporation of cocoa powder at a content of 20-30% in the matrix consisting of PET gave rise to a composite material with good physico-mechanical and chemical properties suitable for use in several sectors. In the construction industry, in particular as wall covering as a replacement for tiles, these x from an economic point of view cost less and compared to clays which consumes enormous amount of energy for the elaboration of ceramics. The study showed that the optimum powder weight proportion for the optimal properties of the composite were achieved at 30% powder weight proportion. The maximum tensile strength of 60.3 MPa, flexural strength of 19.5 MPa, impact strength of 10.3 MPa and water absorption 1.34% were obtained. Water absorption of the tiles increased with the cocoa powder weight. Compare to the ceramic tile this value of water absorption test is in range and show that this composite tile is suitable for use as bathroom tile.