Katsuya Matsumoto, S. Komatsu, M. Ikeda, B. Verlinden, P. Ratchev
{"title":"时效Al-1.0质量%Mg2Si合金中析出相体积分数的定量分析","authors":"Katsuya Matsumoto, S. Komatsu, M. Ikeda, B. Verlinden, P. Ratchev","doi":"10.2320/MATERTRANS1989.41.1275","DOIUrl":null,"url":null,"abstract":"An Al-1.0 mass%Mg 2 Si alloy was aged at 473 K for 36ks. Using the same sample, resistivity (p) measurements, tensile tests and TEM observations were carried out. The volume fraction (V fρ ) of precipitates was estimated from the decrement in resistivity due to aging. Length (λ), diameter (d) and number density (Np) per unit volume of the needle-shaped precipitates were measured on TEM micrographs. Perhaps because of initiation of overaging in the present aging condition, λ and Np showed a wide scatter and differed significantly in two equivalent samples, independently heat treated and tested. However, proof stress and V fρ in the two runs well coincided with each other and the volume fraction estimated from TEM micrographs (V fTEM ) matched within a factor of 2 for the two runs.","PeriodicalId":18264,"journal":{"name":"Materials Transactions Jim","volume":"14 1","pages":"1275-1281"},"PeriodicalIF":0.0000,"publicationDate":"2000-10-20","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"27","resultStr":"{\"title\":\"Quantification of volume fraction of precipitates in an aged Al-1.0 mass%Mg2Si alloy\",\"authors\":\"Katsuya Matsumoto, S. Komatsu, M. Ikeda, B. Verlinden, P. Ratchev\",\"doi\":\"10.2320/MATERTRANS1989.41.1275\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"An Al-1.0 mass%Mg 2 Si alloy was aged at 473 K for 36ks. Using the same sample, resistivity (p) measurements, tensile tests and TEM observations were carried out. The volume fraction (V fρ ) of precipitates was estimated from the decrement in resistivity due to aging. Length (λ), diameter (d) and number density (Np) per unit volume of the needle-shaped precipitates were measured on TEM micrographs. Perhaps because of initiation of overaging in the present aging condition, λ and Np showed a wide scatter and differed significantly in two equivalent samples, independently heat treated and tested. However, proof stress and V fρ in the two runs well coincided with each other and the volume fraction estimated from TEM micrographs (V fTEM ) matched within a factor of 2 for the two runs.\",\"PeriodicalId\":18264,\"journal\":{\"name\":\"Materials Transactions Jim\",\"volume\":\"14 1\",\"pages\":\"1275-1281\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2000-10-20\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"27\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Materials Transactions Jim\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.2320/MATERTRANS1989.41.1275\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials Transactions Jim","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.2320/MATERTRANS1989.41.1275","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Quantification of volume fraction of precipitates in an aged Al-1.0 mass%Mg2Si alloy
An Al-1.0 mass%Mg 2 Si alloy was aged at 473 K for 36ks. Using the same sample, resistivity (p) measurements, tensile tests and TEM observations were carried out. The volume fraction (V fρ ) of precipitates was estimated from the decrement in resistivity due to aging. Length (λ), diameter (d) and number density (Np) per unit volume of the needle-shaped precipitates were measured on TEM micrographs. Perhaps because of initiation of overaging in the present aging condition, λ and Np showed a wide scatter and differed significantly in two equivalent samples, independently heat treated and tested. However, proof stress and V fρ in the two runs well coincided with each other and the volume fraction estimated from TEM micrographs (V fTEM ) matched within a factor of 2 for the two runs.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号