{"title":"分级结构高比表面积氧化铝在FeCrAl合金丝上的生长","authors":"Chandni Rallan, Aaron Akah, P. Hill, A. Garforth","doi":"10.1155/2013/251495","DOIUrl":null,"url":null,"abstract":"The formation of metastable alumina phases due to the oxidation of commercial FeCrAl alloy wires (0.5 mm thickness) at various temperatures and time periods has been examined. Samples were isothermally oxidised in air using a thermogravimetric analyzer (TGA). The morphology of the oxidised samples was analyzed using an Electronic Scanning Electron Microscope (ESEM) and X-ray on the surface analysis was done using an Energy Dispersive X-Ray (EDX) analyzer. The technique of X-Ray Diffraction (XRD) was used to characterize the phase of the oxide growth. The entire study showed that it was possible to grow high-surface area gamma alumina on the FeCrAl alloy wire surfaces when isothermally oxidised above 800°C over several hours.","PeriodicalId":13278,"journal":{"name":"Indian Journal of Materials Science","volume":"47 1","pages":"1-7"},"PeriodicalIF":0.0000,"publicationDate":"2013-12-11","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"2","resultStr":"{\"title\":\"Growth of Hierarchically Structured High-Surface Area Alumina on FeCrAl Alloy Wires\",\"authors\":\"Chandni Rallan, Aaron Akah, P. Hill, A. Garforth\",\"doi\":\"10.1155/2013/251495\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The formation of metastable alumina phases due to the oxidation of commercial FeCrAl alloy wires (0.5 mm thickness) at various temperatures and time periods has been examined. Samples were isothermally oxidised in air using a thermogravimetric analyzer (TGA). The morphology of the oxidised samples was analyzed using an Electronic Scanning Electron Microscope (ESEM) and X-ray on the surface analysis was done using an Energy Dispersive X-Ray (EDX) analyzer. The technique of X-Ray Diffraction (XRD) was used to characterize the phase of the oxide growth. The entire study showed that it was possible to grow high-surface area gamma alumina on the FeCrAl alloy wire surfaces when isothermally oxidised above 800°C over several hours.\",\"PeriodicalId\":13278,\"journal\":{\"name\":\"Indian Journal of Materials Science\",\"volume\":\"47 1\",\"pages\":\"1-7\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2013-12-11\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"2\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Indian Journal of Materials Science\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1155/2013/251495\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Indian Journal of Materials Science","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1155/2013/251495","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Growth of Hierarchically Structured High-Surface Area Alumina on FeCrAl Alloy Wires
The formation of metastable alumina phases due to the oxidation of commercial FeCrAl alloy wires (0.5 mm thickness) at various temperatures and time periods has been examined. Samples were isothermally oxidised in air using a thermogravimetric analyzer (TGA). The morphology of the oxidised samples was analyzed using an Electronic Scanning Electron Microscope (ESEM) and X-ray on the surface analysis was done using an Energy Dispersive X-Ray (EDX) analyzer. The technique of X-Ray Diffraction (XRD) was used to characterize the phase of the oxide growth. The entire study showed that it was possible to grow high-surface area gamma alumina on the FeCrAl alloy wire surfaces when isothermally oxidised above 800°C over several hours.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号