{"title":"层高对FDM打印试样抗拉强度的影响","authors":"Ł. Miazio","doi":"10.31648/ts.6297","DOIUrl":null,"url":null,"abstract":"This article analyzes the influence of layer height on the tensile strength of PLA specimens printed in the Fused Deposition Modeling (FDM) technology. The maximum breaking force of specimens with 30% and 100% infill density was determined at layer height of 0.05 mm, 0.1 mm, 0.2 mm and 0.3 mm. In the case of 30% infill, the highest value of the force was obtained for a layer with a height of 0.05 mm (which corresponds to 22.7 MPa), and for a 100% infill for a layer of 0.2 (which corresponds to 40 MPa). Over this layer height of 0.2 mm is the most polyoptimal due to the time prints and strength (which corresponds to 19.7 MPa).","PeriodicalId":41669,"journal":{"name":"Archives for Technical Sciences","volume":"4 1","pages":""},"PeriodicalIF":0.2000,"publicationDate":"2021-08-09","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"The influence of layer height on the tensile strength of specimens printed in the FDM technology\",\"authors\":\"Ł. Miazio\",\"doi\":\"10.31648/ts.6297\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"This article analyzes the influence of layer height on the tensile strength of PLA specimens printed in the Fused Deposition Modeling (FDM) technology. The maximum breaking force of specimens with 30% and 100% infill density was determined at layer height of 0.05 mm, 0.1 mm, 0.2 mm and 0.3 mm. In the case of 30% infill, the highest value of the force was obtained for a layer with a height of 0.05 mm (which corresponds to 22.7 MPa), and for a 100% infill for a layer of 0.2 (which corresponds to 40 MPa). Over this layer height of 0.2 mm is the most polyoptimal due to the time prints and strength (which corresponds to 19.7 MPa).\",\"PeriodicalId\":41669,\"journal\":{\"name\":\"Archives for Technical Sciences\",\"volume\":\"4 1\",\"pages\":\"\"},\"PeriodicalIF\":0.2000,\"publicationDate\":\"2021-08-09\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Archives for Technical Sciences\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.31648/ts.6297\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q4\",\"JCRName\":\"ENGINEERING, GEOLOGICAL\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Archives for Technical Sciences","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.31648/ts.6297","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"ENGINEERING, GEOLOGICAL","Score":null,"Total":0}
The influence of layer height on the tensile strength of specimens printed in the FDM technology
This article analyzes the influence of layer height on the tensile strength of PLA specimens printed in the Fused Deposition Modeling (FDM) technology. The maximum breaking force of specimens with 30% and 100% infill density was determined at layer height of 0.05 mm, 0.1 mm, 0.2 mm and 0.3 mm. In the case of 30% infill, the highest value of the force was obtained for a layer with a height of 0.05 mm (which corresponds to 22.7 MPa), and for a 100% infill for a layer of 0.2 (which corresponds to 40 MPa). Over this layer height of 0.2 mm is the most polyoptimal due to the time prints and strength (which corresponds to 19.7 MPa).
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号