硼胺基表面改性二氧化硅填料的性能

M. Elvira, A. Macías, J. L. Oteo, Joaquín Royo, J. Rubio
{"title":"硼胺基表面改性二氧化硅填料的性能","authors":"M. Elvira, A. Macías, J. L. Oteo, Joaquín Royo, J. Rubio","doi":"10.1002/APMC.1994.052170111","DOIUrl":null,"url":null,"abstract":"The behaviour of silica fillers modified with primary boron-amine groups has been studied under different reaction conditions. The filler with the best reinforcing properties was used to compare two different vulcanization systems: an efficient vulcanization system, EV, which is the recommended ISO Standards method to study the reinforcing behaviour of new silicas, and a conventional vulcanization system. \n \n \n \nThe results indicate that the best properties are obtained with silica treated for 3 h at 500°C, reaction conditions which fix most of the primary boron-amine groups. Using the EV system, the properties of this modified silica are similar to those of silane-modified silica, and in some cases better than those obtained with a conventional vulcanization system. In all cases, the boron-amination treatment significantly improves the behaviour of precipitated silica as a reinforcing filler. \n \n \n \nDas Verhalten von mit primaren Boramingruppen modifizierten Silikat-Fullstoffen wurde unter verschiedenen Reaktionsbedingungen untersucht. Der Fullstoff mit den besten Verstarkungseigenschaften wurde eingesetzt, um zwei unterschiedliche Vulkanisationssysteme zu vergleichen: ein wirksames Vulkanisationsverfahren (EV), das nach ISO als Methode zur Untersuchung des Verstarkungsverhaltens neuer Silikate empfohlen wird, sowie ein konventionelles Verfahren. Die besten Ergebnisse werden mit Silikat erhalten, welches 3 h bei 500°C behandelt wurde; unter diesen Bedingungen werden die meisten der primaren Boramingruppen fixiert. Die Eigenschaften des nach dem EV-Verfahren modifizierten Silikats ahneln denen von mit Silan modifizierten Silikaten und sind in einigen Fallen besser als jene, welche nach dem konventionellen Verfahren erhalten werden. In allen Fallen wird die verstarkende Wirkung von gefallten Silikat-Fullstoffen durch die Boraminbehandlung verbessert.","PeriodicalId":7808,"journal":{"name":"Angewandte Makromolekulare Chemie","volume":"79 1","pages":"107-117"},"PeriodicalIF":0.0000,"publicationDate":"1994-04-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Behaviour of a silica filler surface‐modified with boron‐amine groups\",\"authors\":\"M. Elvira, A. Macías, J. L. Oteo, Joaquín Royo, J. Rubio\",\"doi\":\"10.1002/APMC.1994.052170111\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The behaviour of silica fillers modified with primary boron-amine groups has been studied under different reaction conditions. The filler with the best reinforcing properties was used to compare two different vulcanization systems: an efficient vulcanization system, EV, which is the recommended ISO Standards method to study the reinforcing behaviour of new silicas, and a conventional vulcanization system. \\n \\n \\n \\nThe results indicate that the best properties are obtained with silica treated for 3 h at 500°C, reaction conditions which fix most of the primary boron-amine groups. Using the EV system, the properties of this modified silica are similar to those of silane-modified silica, and in some cases better than those obtained with a conventional vulcanization system. In all cases, the boron-amination treatment significantly improves the behaviour of precipitated silica as a reinforcing filler. \\n \\n \\n \\nDas Verhalten von mit primaren Boramingruppen modifizierten Silikat-Fullstoffen wurde unter verschiedenen Reaktionsbedingungen untersucht. Der Fullstoff mit den besten Verstarkungseigenschaften wurde eingesetzt, um zwei unterschiedliche Vulkanisationssysteme zu vergleichen: ein wirksames Vulkanisationsverfahren (EV), das nach ISO als Methode zur Untersuchung des Verstarkungsverhaltens neuer Silikate empfohlen wird, sowie ein konventionelles Verfahren. Die besten Ergebnisse werden mit Silikat erhalten, welches 3 h bei 500°C behandelt wurde; unter diesen Bedingungen werden die meisten der primaren Boramingruppen fixiert. Die Eigenschaften des nach dem EV-Verfahren modifizierten Silikats ahneln denen von mit Silan modifizierten Silikaten und sind in einigen Fallen besser als jene, welche nach dem konventionellen Verfahren erhalten werden. In allen Fallen wird die verstarkende Wirkung von gefallten Silikat-Fullstoffen durch die Boraminbehandlung verbessert.\",\"PeriodicalId\":7808,\"journal\":{\"name\":\"Angewandte Makromolekulare Chemie\",\"volume\":\"79 1\",\"pages\":\"107-117\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"1994-04-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Angewandte Makromolekulare Chemie\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1002/APMC.1994.052170111\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Angewandte Makromolekulare Chemie","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1002/APMC.1994.052170111","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0

摘要

研究了伯硼胺基改性二氧化硅填料在不同反应条件下的性能。采用补强性能最好的填料对两种不同的硫化体系进行了比较:一种是高效硫化体系EV,这是ISO标准推荐的研究新型二氧化硅补强性能的方法,另一种是传统的硫化体系。结果表明,二氧化硅在500℃下处理3 h得到的性能最好,反应条件可以固定大部分伯硼胺基。使用EV体系,这种改性二氧化硅的性能与硅烷改性二氧化硅的性能相似,在某些情况下比使用常规硫化体系得到的性能更好。在所有情况下,硼胺化处理显著改善了作为补强填料的沉淀二氧化硅的性能。Das Verhalten von mit primary Boramingruppen modififient silkat - fullstoffen wurde unschiedenen Reaktionsbedingungen untersut。Der Fullstoff mitden besten Verstarkungseigenschaften wurde eingesetzt, um zwei unschiedliche Vulkanisationssysteme zuvergleichen: ein workksames Vulkanisationsverfahren (EV),也称为Methode zur Untersuchung des Verstarkungsverhaltens neuer silica employeenward, sowie ein konventionelles Verfahren。Die besten Ergebnisse werden mit silitkat erhalten, welches 3 h behandelt wurde 500℃;underen Bedingungen werden die meisten der primaren boringgruppen fixert。Die Eigenschaften des nach dem EV-Verfahren modififitersilikats - nehniln denen von mit Silan modififitersilikaten and sind in inteligen Fallen besser也jene, welche nach dem conventionellen Verfahren erhalten werden。在秋天的风die verstarkende Wirkung von gefallten silkat - fullstoffen durch die Boraminbehandlung verbessert。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
Behaviour of a silica filler surface‐modified with boron‐amine groups
The behaviour of silica fillers modified with primary boron-amine groups has been studied under different reaction conditions. The filler with the best reinforcing properties was used to compare two different vulcanization systems: an efficient vulcanization system, EV, which is the recommended ISO Standards method to study the reinforcing behaviour of new silicas, and a conventional vulcanization system. The results indicate that the best properties are obtained with silica treated for 3 h at 500°C, reaction conditions which fix most of the primary boron-amine groups. Using the EV system, the properties of this modified silica are similar to those of silane-modified silica, and in some cases better than those obtained with a conventional vulcanization system. In all cases, the boron-amination treatment significantly improves the behaviour of precipitated silica as a reinforcing filler. Das Verhalten von mit primaren Boramingruppen modifizierten Silikat-Fullstoffen wurde unter verschiedenen Reaktionsbedingungen untersucht. Der Fullstoff mit den besten Verstarkungseigenschaften wurde eingesetzt, um zwei unterschiedliche Vulkanisationssysteme zu vergleichen: ein wirksames Vulkanisationsverfahren (EV), das nach ISO als Methode zur Untersuchung des Verstarkungsverhaltens neuer Silikate empfohlen wird, sowie ein konventionelles Verfahren. Die besten Ergebnisse werden mit Silikat erhalten, welches 3 h bei 500°C behandelt wurde; unter diesen Bedingungen werden die meisten der primaren Boramingruppen fixiert. Die Eigenschaften des nach dem EV-Verfahren modifizierten Silikats ahneln denen von mit Silan modifizierten Silikaten und sind in einigen Fallen besser als jene, welche nach dem konventionellen Verfahren erhalten werden. In allen Fallen wird die verstarkende Wirkung von gefallten Silikat-Fullstoffen durch die Boraminbehandlung verbessert.
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
自引率
0.00%
发文量
0
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
确定
请完成安全验证×
copy
已复制链接
快去分享给好友吧!
我知道了
右上角分享
点击右上角分享
0
联系我们:info@booksci.cn Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。 Copyright © 2023 布克学术 All rights reserved.
京ICP备2023020795号-1
ghs 京公网安备 11010802042870号
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术官方微信