Yao-Can Zhu, Y. Zhang, X. Li, K. Fujita, N. Iwamoto
{"title":"磁控溅射SiO2涂层对γ-TiAl合金循环氧化行为的影响","authors":"Yao-Can Zhu, Y. Zhang, X. Li, K. Fujita, N. Iwamoto","doi":"10.2320/MATERTRANS1989.41.1118","DOIUrl":null,"url":null,"abstract":"A SiO 2 coating of about 2 μm was deposited onto γ-TiAl alloys by using a magnetron-sputtering coating method. The cyclic oxidation behavior of γ-TiAl alloys was investigated at 1123 K in air. The uncoated γ-TiAl specimen showed a high oxidation rate during the initially transient period of up to 220 ks, after which, a rapid mass loss was observed due to the partial scale spallation. In contrast, the SiO 2 -coated TiAl specimen exhibited an extremely low oxidation rate. It was found that the SiO 2 coating acted as an external barrier coating, thereby being capable of significantly suppressing the oxidation of γ-TiAl alloys.","PeriodicalId":18264,"journal":{"name":"Materials Transactions Jim","volume":"219 1","pages":"1118-1120"},"PeriodicalIF":0.0000,"publicationDate":"2000-09-20","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"16","resultStr":"{\"title\":\"The Influence of Magnetron-sputtered SiO2 Coatings on the Cyclic Oxidation Behavior of γ-TiAl Alloys\",\"authors\":\"Yao-Can Zhu, Y. Zhang, X. Li, K. Fujita, N. Iwamoto\",\"doi\":\"10.2320/MATERTRANS1989.41.1118\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"A SiO 2 coating of about 2 μm was deposited onto γ-TiAl alloys by using a magnetron-sputtering coating method. The cyclic oxidation behavior of γ-TiAl alloys was investigated at 1123 K in air. The uncoated γ-TiAl specimen showed a high oxidation rate during the initially transient period of up to 220 ks, after which, a rapid mass loss was observed due to the partial scale spallation. In contrast, the SiO 2 -coated TiAl specimen exhibited an extremely low oxidation rate. It was found that the SiO 2 coating acted as an external barrier coating, thereby being capable of significantly suppressing the oxidation of γ-TiAl alloys.\",\"PeriodicalId\":18264,\"journal\":{\"name\":\"Materials Transactions Jim\",\"volume\":\"219 1\",\"pages\":\"1118-1120\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2000-09-20\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"16\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Materials Transactions Jim\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.2320/MATERTRANS1989.41.1118\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials Transactions Jim","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.2320/MATERTRANS1989.41.1118","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
The Influence of Magnetron-sputtered SiO2 Coatings on the Cyclic Oxidation Behavior of γ-TiAl Alloys
A SiO 2 coating of about 2 μm was deposited onto γ-TiAl alloys by using a magnetron-sputtering coating method. The cyclic oxidation behavior of γ-TiAl alloys was investigated at 1123 K in air. The uncoated γ-TiAl specimen showed a high oxidation rate during the initially transient period of up to 220 ks, after which, a rapid mass loss was observed due to the partial scale spallation. In contrast, the SiO 2 -coated TiAl specimen exhibited an extremely low oxidation rate. It was found that the SiO 2 coating acted as an external barrier coating, thereby being capable of significantly suppressing the oxidation of γ-TiAl alloys.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号