Structural Analysis and Magnetic Properties of FeCo Alloys Obtained by Mechanical Alloying

A systematic study on the structural and magnetic properties of alloys (, in wt. percent) obtained by mechanical alloying is presented. Elemental powders of Fe and Co mixed in an adequate weight ratio were milled at room temperature in a shaker mixer mill using vials and balls of hardened steel as milling media with a ball : powder weight ratio of 12 : 1. The mixtures were milled for 3 h. The results show that, after milling, for almost all the composition (up to ), solid solutions based on bcc structures were obtained. For Co-rich alloys (), different phases were found, revealing the formation of a metastable intermetallic phase (FeCo, wairauite) together with fcc-Co and hcp-Co phases. The specific saturation magnetization increases by increasing Co content, reaching a maximum value of 225 emu/g for hcp-Fe70Co30, and then it shows a diminution up to 154 emu/g for bcc-Fe30Co70. All studied alloys () present low coercivity, in the range from 0 to 65 Oe, which is lower than reported. The coercivity increases with the increment in Co, reaching a maximum of 64.1 Oe for Fe40Co60. After that, the coercivity falls up to 24.5 Oe for Co-rich alloys, which make them a very low coercive material.