Effect of Nanoalumina on the Electrochemical and Mechanical Properties of Waterborne Polyurethane Composite Coatings

A nanocomposite coating was formed by incorporating nanoalumina pigment in a waterborne polyurethane dispersion (WPUD) to different loading levels (0.1% and 1.0% by weight). Electrochemical performance of the nanocomposite coating was evaluated by applying these nanomodified coatings on mild steel substrate and exposing them to salt-spray, humidity, and accelerated UV weathering. The surface morphology of the composite coating was evaluated using various analytical techniques. SEM and AFM were used to investigate the dispersion of nanoalumina pigment and surface morphological changes of the nanomodified coating, before and after exposure to the test environment. Mechanical properties like scratch resistance were studied by using nanoscratch technique (Nanoindenter TI-900, Hysitron Inc, USA) and hardness using pencil hardness test method. The results showed an improvement in the corrosion, UV weathering, and mechanical properties of the coatings at lower concentration (0.1% by wt), indicating the positive effect of addition of nanoalumina pigment to the coating.