{"title":"不同氧化锌含量纳米晶多组分(Co,Cu,Mg,Ni,Zn)O金属氧化物合成过程中的相演化","authors":"N. Usharani, R. N. Kumar, S. Bhattacharya","doi":"10.11159/ICNNFC17.143","DOIUrl":null,"url":null,"abstract":"Extended Abstract Nanocrystalline ceramics have great potential for applications in electronics, sensors and energy-related areas due to their remarkable functional properties. However, only doped, co-doped and binary ceramics have been extensively studied, while the area of equimolar, multicomponent ceramics has been a largely unexplored field until recently [1]–[3]. In this investigation, a multicomponent nanocrystalline ceramic oxide, (Co,Cu,Mg,Ni,Zn)O, was synthesised with the primary intention of studying the type and stability of the phases formed with systematically varying zinc oxide content. The individual components were selected on the basis of Pauling’s rules in order to maximise the probability of single phase formation. All these elements have a +2 oxidation state in their stable oxide form. While the oxides of cobalt, magnesium and nickel have a stable rocksalt crystal structure, zinc oxide stabilizes in the wurzite structure and copper has a stable monoclinic structure (a distorted rocksalt structure, due to the Jahn-Teller effect). Therefore, it could be expected that copper and zinc would distribute themselves in the stable lattice structure of the other rocksalt oxides and form a solid solution within the 5 component system, even though it has been reported that in the binary (Ni,Cu)O system, the dominant Jahn-Teller effect leads to the formation of a distorted cubic structure [4]. Based on this premise, a bottom-up, nebulised spray pyrolysis (NSP) approach was selected for synthesis. NSP is a relatively rapid process with adequate residence time which yields clean and stable equilibrium (or near-equilibrium) phases of the product. The process is also industrially scalable. Nitrates of the selected cations were used as precursors and the individual precursor quantities were adjusted in order to maintain the requisite final compositions with de-ionised water as the solvent. X-ray diffraction (XRD) of the as-synthesized powders confirmed the presence of single phase cubic rocksalt structure in the fm3̅m space group for all the compositions. The variation of the synthesis temperature shows a decreasing trend from 1400 C to 1100 C for uniform increase in the concentration of ZnO from 4% to equimolar composition because of increasing configurational entropy towards equimolar concentrations. This observation could be also due to the decrease in Jahn-Teller effect with decrease in CuO concentration. The crystallite size calculated using Scherrer formula shows a decrease from 48 nm for 4% ZnO to 20 nm for 20% ZnO in a linear fashion since ZnO has a different crystal structure, necessitating more energy requirement to dissolve ZnO in rocksalt lattice leaving lesser energy for crystallite growth. Also with increasing ZnO concentration, its dissimilar crystal structure hinders the diffusion of isostructured components leading to lesser crystallite growth.[5]. Scanning electron microscopy (SEM) revealed the particles to have broken shell like morphology and energy dispersive spectroscopy associated with the SEM confirmed the composition.","PeriodicalId":31009,"journal":{"name":"RAN","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2017-04-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"1","resultStr":"{\"title\":\"Phase Evolution During Synthesis of Nanocrystalline Multicomponent (Co,Cu,Mg,Ni,Zn)O Metal Oxides with Varying ZnO Content\",\"authors\":\"N. Usharani, R. N. Kumar, S. Bhattacharya\",\"doi\":\"10.11159/ICNNFC17.143\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Extended Abstract Nanocrystalline ceramics have great potential for applications in electronics, sensors and energy-related areas due to their remarkable functional properties. However, only doped, co-doped and binary ceramics have been extensively studied, while the area of equimolar, multicomponent ceramics has been a largely unexplored field until recently [1]–[3]. In this investigation, a multicomponent nanocrystalline ceramic oxide, (Co,Cu,Mg,Ni,Zn)O, was synthesised with the primary intention of studying the type and stability of the phases formed with systematically varying zinc oxide content. The individual components were selected on the basis of Pauling’s rules in order to maximise the probability of single phase formation. All these elements have a +2 oxidation state in their stable oxide form. While the oxides of cobalt, magnesium and nickel have a stable rocksalt crystal structure, zinc oxide stabilizes in the wurzite structure and copper has a stable monoclinic structure (a distorted rocksalt structure, due to the Jahn-Teller effect). Therefore, it could be expected that copper and zinc would distribute themselves in the stable lattice structure of the other rocksalt oxides and form a solid solution within the 5 component system, even though it has been reported that in the binary (Ni,Cu)O system, the dominant Jahn-Teller effect leads to the formation of a distorted cubic structure [4]. Based on this premise, a bottom-up, nebulised spray pyrolysis (NSP) approach was selected for synthesis. NSP is a relatively rapid process with adequate residence time which yields clean and stable equilibrium (or near-equilibrium) phases of the product. The process is also industrially scalable. Nitrates of the selected cations were used as precursors and the individual precursor quantities were adjusted in order to maintain the requisite final compositions with de-ionised water as the solvent. X-ray diffraction (XRD) of the as-synthesized powders confirmed the presence of single phase cubic rocksalt structure in the fm3̅m space group for all the compositions. The variation of the synthesis temperature shows a decreasing trend from 1400 C to 1100 C for uniform increase in the concentration of ZnO from 4% to equimolar composition because of increasing configurational entropy towards equimolar concentrations. This observation could be also due to the decrease in Jahn-Teller effect with decrease in CuO concentration. The crystallite size calculated using Scherrer formula shows a decrease from 48 nm for 4% ZnO to 20 nm for 20% ZnO in a linear fashion since ZnO has a different crystal structure, necessitating more energy requirement to dissolve ZnO in rocksalt lattice leaving lesser energy for crystallite growth. Also with increasing ZnO concentration, its dissimilar crystal structure hinders the diffusion of isostructured components leading to lesser crystallite growth.[5]. Scanning electron microscopy (SEM) revealed the particles to have broken shell like morphology and energy dispersive spectroscopy associated with the SEM confirmed the composition.\",\"PeriodicalId\":31009,\"journal\":{\"name\":\"RAN\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2017-04-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"1\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"RAN\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.11159/ICNNFC17.143\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"RAN","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.11159/ICNNFC17.143","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Phase Evolution During Synthesis of Nanocrystalline Multicomponent (Co,Cu,Mg,Ni,Zn)O Metal Oxides with Varying ZnO Content
Extended Abstract Nanocrystalline ceramics have great potential for applications in electronics, sensors and energy-related areas due to their remarkable functional properties. However, only doped, co-doped and binary ceramics have been extensively studied, while the area of equimolar, multicomponent ceramics has been a largely unexplored field until recently [1]–[3]. In this investigation, a multicomponent nanocrystalline ceramic oxide, (Co,Cu,Mg,Ni,Zn)O, was synthesised with the primary intention of studying the type and stability of the phases formed with systematically varying zinc oxide content. The individual components were selected on the basis of Pauling’s rules in order to maximise the probability of single phase formation. All these elements have a +2 oxidation state in their stable oxide form. While the oxides of cobalt, magnesium and nickel have a stable rocksalt crystal structure, zinc oxide stabilizes in the wurzite structure and copper has a stable monoclinic structure (a distorted rocksalt structure, due to the Jahn-Teller effect). Therefore, it could be expected that copper and zinc would distribute themselves in the stable lattice structure of the other rocksalt oxides and form a solid solution within the 5 component system, even though it has been reported that in the binary (Ni,Cu)O system, the dominant Jahn-Teller effect leads to the formation of a distorted cubic structure [4]. Based on this premise, a bottom-up, nebulised spray pyrolysis (NSP) approach was selected for synthesis. NSP is a relatively rapid process with adequate residence time which yields clean and stable equilibrium (or near-equilibrium) phases of the product. The process is also industrially scalable. Nitrates of the selected cations were used as precursors and the individual precursor quantities were adjusted in order to maintain the requisite final compositions with de-ionised water as the solvent. X-ray diffraction (XRD) of the as-synthesized powders confirmed the presence of single phase cubic rocksalt structure in the fm3̅m space group for all the compositions. The variation of the synthesis temperature shows a decreasing trend from 1400 C to 1100 C for uniform increase in the concentration of ZnO from 4% to equimolar composition because of increasing configurational entropy towards equimolar concentrations. This observation could be also due to the decrease in Jahn-Teller effect with decrease in CuO concentration. The crystallite size calculated using Scherrer formula shows a decrease from 48 nm for 4% ZnO to 20 nm for 20% ZnO in a linear fashion since ZnO has a different crystal structure, necessitating more energy requirement to dissolve ZnO in rocksalt lattice leaving lesser energy for crystallite growth. Also with increasing ZnO concentration, its dissimilar crystal structure hinders the diffusion of isostructured components leading to lesser crystallite growth.[5]. Scanning electron microscopy (SEM) revealed the particles to have broken shell like morphology and energy dispersive spectroscopy associated with the SEM confirmed the composition.