Influence of Morphology Pattern of Genuine Damascus Steel on the Nature of Relief of Fracture Surfaces

It has been revealed that the structure of the transverse and longitudinal parts of the genuine Damascus knife of the XVIII century consists of troos-tite-carbide of the banding. The microhardness of the troostite layers is 450 HV; the carbide layers reach 950 HV. It is shown that such a banding structure in hardness will have a huge impact on the formation of a naturally patterned genuine Damascus structure. It is established that the form of the main drawings of the genuine Damascus pattern consists of separate elements of the topographic contour: hollows, hills, saddles, crosses and wavy dunes. It is shown that the damask pattern is a set of individual elements of the macrostructure alternating in a disordered form on different local areas of the surface. It is established that the destruction of genuine Damascus steels occurs under the action of two or more mechanisms, during the implementation of which traces remain on the surface of the fractures in the form of relief details of a mixed type. The mechanisms of mixed destruction are a combination of intragrain cleavage, micropore fusion and intergrain cracking. It is established that in order to implement the mechanism of separation of the main crack in the direction of the chopping blow, an optimum is required in the dispersion of troostite (61.8%) and carbide (38.2%) layers in genuine Damascus steel, the ratio of their volumes obeys the golden section rule. It is established that the damask pattern, consisting of elements of sinuous lines of a topographic contour, does not significantly affect the level of mechanical properties. This factor is a category of the quality of banding structures in genuine Damascus steel.