Promoted Catalytic Properties of Acetone over Cerium-Modified Mullite Catalyst YMn2O5

Mullite catalysts have become one of the most widely studied catalysts due to their highly stable structure and unique coordination with oxygen. In this work, Ce-modified mullite-type oxides Y 1-x Ce x Mn 2 O 5 have been prepared by sol-gel method to explore their Ce doping amount-dependent catalytic performance for acetone elimination. Experimental results confirm that Y 0.9 Ce 0.1 Mn 2 O 5 had optimum acetone oxidation activity, completely achieving 100% acetone conversion at 120 ° C under the reaction conditions of acetone concentration = 1000 ppm, 20 vol% O 2 /N 2 and WHSV = 36000 mL g –1 h –1 . This excellent catalytic activity comes from its larger specific surface area and higher Mn 4+ /Mn 3+ molar ratio. XRD and TEM results show that YMn 2 O 5 and CeO 2 phases form a multiphase oxide and interfacial structure. XPS results show that the content of doped CeO 2 mainly affects the surface adsorbed oxygen (Oads) and Mn 4+ content of the catalyst. Manganese species with higher chemical states are indeed more favorable for oxidation reactions on manganese-based catalysts. In addition, the reduction temperature of mixed oxides shifts to the lower temperature region, indicating that manganese and cerium oxides are more reducible, where the mobility of oxygen species is greatly enhanced. Y 0.9 Ce 0.1 Mn 2 O 5 also exhibits strong long-term stability and has good resistance to acetone elimination, showing excellent potential in eliminating acetone.