从氢氧化镍钴混合沉淀物中提取镍

Q4 Engineering

Scientific Mining Journal Pub Date : 2019-03-01 DOI:10.30797/MADENCILIK.537644

Sait Kurşunoğlu

{"title":"从氢氧化镍钴混合沉淀物中提取镍","authors":"Sait Kurşunoğlu","doi":"10.30797/MADENCILIK.537644","DOIUrl":null,"url":null,"abstract":"The extraction of nickel from a mixed nickel-cobalt hydroxide precipitate (MHP) was conceived and experimentally explored. The effect of sulphuric acid concentration, leaching time, leaching temperature and stirring speed on nickel extraction was investigated. After 60 min leaching time, more than 90% of nickel and approximately 80% of cobalt were taken into the leach solution under the following conditions: 0.75M sulphuric acid concentration, 30°C leaching temperature and 400 rpm stirring speed. pH of the leach slurry was determined as 1.23 under the conditions explored. It was observed that there is no beneficial effect of leaching temperature and stirring speed on the extraction of nickel from the MHP sample. The XRD pattern of the fresh MHP sample revealed the data and peak of the sample widening which is indicative of amorphous solid structure.","PeriodicalId":37481,"journal":{"name":"Scientific Mining Journal","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2019-03-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"3","resultStr":"{\"title\":\"EXTRACTION OF NICKEL FROM A MIXED NICKEL-COBALT HYDROXIDE PRECIPITATE\",\"authors\":\"Sait Kurşunoğlu\",\"doi\":\"10.30797/MADENCILIK.537644\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The extraction of nickel from a mixed nickel-cobalt hydroxide precipitate (MHP) was conceived and experimentally explored. The effect of sulphuric acid concentration, leaching time, leaching temperature and stirring speed on nickel extraction was investigated. After 60 min leaching time, more than 90% of nickel and approximately 80% of cobalt were taken into the leach solution under the following conditions: 0.75M sulphuric acid concentration, 30°C leaching temperature and 400 rpm stirring speed. pH of the leach slurry was determined as 1.23 under the conditions explored. It was observed that there is no beneficial effect of leaching temperature and stirring speed on the extraction of nickel from the MHP sample. The XRD pattern of the fresh MHP sample revealed the data and peak of the sample widening which is indicative of amorphous solid structure.\",\"PeriodicalId\":37481,\"journal\":{\"name\":\"Scientific Mining Journal\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2019-03-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"3\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Scientific Mining Journal\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.30797/MADENCILIK.537644\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q4\",\"JCRName\":\"Engineering\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Scientific Mining Journal","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.30797/MADENCILIK.537644","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"Engineering","Score":null,"Total":0}

引用次数: 3

摘要

设想并实验探索了从混合镍钴氢氧化物沉淀物（MHP）中提取镍的方法。研究了硫酸浓度、浸出时间、浸出温度和搅拌速度对镍萃取的影响。在60分钟的浸出时间后，在以下条件下，将90%以上的镍和约80%的钴带入浸出溶液：0.75M硫酸浓度、30°C浸出温度和400rpm搅拌速度。在所探索的条件下，确定浸出浆液的pH为1.23。观察到浸出温度和搅拌速度对从MHP样品中提取镍没有有利影响。新鲜MHP样品的XRD图谱揭示了样品的数据和峰变宽，这表明无定形固体结构。

本文章由计算机程序翻译，如有差异，请以英文原文为准。

查看原文本刊更多论文

EXTRACTION OF NICKEL FROM A MIXED NICKEL-COBALT HYDROXIDE PRECIPITATE

The extraction of nickel from a mixed nickel-cobalt hydroxide precipitate (MHP) was conceived and experimentally explored. The effect of sulphuric acid concentration, leaching time, leaching temperature and stirring speed on nickel extraction was investigated. After 60 min leaching time, more than 90% of nickel and approximately 80% of cobalt were taken into the leach solution under the following conditions: 0.75M sulphuric acid concentration, 30°C leaching temperature and 400 rpm stirring speed. pH of the leach slurry was determined as 1.23 under the conditions explored. It was observed that there is no beneficial effect of leaching temperature and stirring speed on the extraction of nickel from the MHP sample. The XRD pattern of the fresh MHP sample revealed the data and peak of the sample widening which is indicative of amorphous solid structure.

求助全文

通过发布文献求助，成功后即可免费获取论文全文。去求助

来源期刊

Scientific Mining Journal Engineering-Industrial and Manufacturing Engineering

CiteScore

0.60

自引率

0.00%

发文量

期刊介绍： Scientific Mining Journal, which is published i n open access electronic environment and i n printed, is a periodical scientific journal of Union of Chambers of Turkish Engineers and Architects Chamber of Mining Engineers. The name of the journal was "Mining" until June 2016 and it has been changed to "Scientific Mining Journal" since September 2016 because it can be confused with popular journals with similar names and the ISSN number has been updated from 0024-9416 to 2564-7024. Scientific Mining Journal, published four times a year (March-June-September-December), aims to disseminate original scientific studies which are conducted according to the scientific norms and publication ethics at national and international scale, to scientists, mining engineers, the public; and thus to share scientific knowledge with society. The journal is in both Turkish and English. The journal covers theoretical, experimental, and applied research articles, which reflects the findings and results of an original research i n the field of mining engineering; review articles, which assess, evaluates, and interprets the findings of a comprehensive review of sufficient number of scientific articles and summarize them at present information and technology level; technical notes, which may be defined as a short article that describes a novel methodology o r technique; a case studies, which are based on the theoretical o r real professional practice and involves systematic data collection and analysis.