Optimization of structural parameters on hollow spherical cells manufactured by Fused Deposition Modeling (FDM) using Taguchi method

There is a growing need for 3D printing of polymer structures in a cost-effective way and green. This study presents an experimental approach to investigate structural parameters effects on mechanical properties of polylactic acid (PLA) hollow-sphere structures manufactured with fused deposition modeling (FDM). The mechanical behavior characteristics of square_hexagonal stacking, closed_open porosity and parallel_perpendicular compression direction compared to the direction of manufacture under quasi-static uniaxial compression are examined using Taguchi method. The S/N ratio analysis and the Analysis of Variance (ANOVA) were used to find the optimal parameters that improve the mechanical properties (Young modulus, yield strength) and to provide a significant ranking of the different parameters analyzed in this paper. It was found that the optimum level and significance of each process parameter vary for “hexagonal cells,” “open porosity” and “parallel direction.” The optimal values of the results give a Young modulus E of 90.12 MPa and a yield strength σ y of 3 MPa. Furthermore, the experimental results further reveal that the porous structure with the loading direction that is parallel to the direction of manufacture, has a higher strength and a progressive collapse of the cells to those with a perpendicular direction.