{"title":"元素粉末制备nb改性近β钛合金的粉末冶金工艺研究","authors":"V. Opini, J. B. Fogagnolo, V. A. Borrás, R. Caram, J. Soyama","doi":"10.1080/00325899.2023.2228093","DOIUrl":null,"url":null,"abstract":"ABSTRACT Near β Ti alloys typically show high specific strength and provide a wide spectrum of mechanical properties with different heat treatments. In this work, a commercial near β Ti alloy Ti-5553 (Ti-5Al-5V-5Mo-3Cr-0.5Fe) was prepared through powder metallurgy using the blended elemental powder approach. Additionally, alloy modifications with 6 wt.% Nb (Ti-6Nb-5Al-2.5V-5Mo-3Cr-0.5Fe) and 12 wt.% Nb (Ti-12Nb-5Al-5Mo-3Cr-0.5Fe) were investigated. Specimens were prepared by uniaxial cold compaction of blended powders at room temperature with sintering conducted at 1300°C for 2 h under Ar atmosphere. Microstructure investigation revealed reasonable homogenisation of alloying elements and colony sizes in the order of 80-100 μm with porosity below 10%. Moreover, the bending strength of as-sintered Ti-12Nb-5Al-5Mo-3Cr-0.5Fe was about 850 MPa and the micro-Vickers hardness was approximately 370 HV. The alloy modifications with Nb increased strength without loss in flexural strain.","PeriodicalId":20392,"journal":{"name":"Powder Metallurgy","volume":null,"pages":null},"PeriodicalIF":1.9000,"publicationDate":"2023-06-26","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Powder metallurgy processing of Nb-modified near β titanium alloys prepared with elemental powders\",\"authors\":\"V. Opini, J. B. Fogagnolo, V. A. Borrás, R. Caram, J. Soyama\",\"doi\":\"10.1080/00325899.2023.2228093\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"ABSTRACT Near β Ti alloys typically show high specific strength and provide a wide spectrum of mechanical properties with different heat treatments. In this work, a commercial near β Ti alloy Ti-5553 (Ti-5Al-5V-5Mo-3Cr-0.5Fe) was prepared through powder metallurgy using the blended elemental powder approach. Additionally, alloy modifications with 6 wt.% Nb (Ti-6Nb-5Al-2.5V-5Mo-3Cr-0.5Fe) and 12 wt.% Nb (Ti-12Nb-5Al-5Mo-3Cr-0.5Fe) were investigated. Specimens were prepared by uniaxial cold compaction of blended powders at room temperature with sintering conducted at 1300°C for 2 h under Ar atmosphere. Microstructure investigation revealed reasonable homogenisation of alloying elements and colony sizes in the order of 80-100 μm with porosity below 10%. Moreover, the bending strength of as-sintered Ti-12Nb-5Al-5Mo-3Cr-0.5Fe was about 850 MPa and the micro-Vickers hardness was approximately 370 HV. The alloy modifications with Nb increased strength without loss in flexural strain.\",\"PeriodicalId\":20392,\"journal\":{\"name\":\"Powder Metallurgy\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":1.9000,\"publicationDate\":\"2023-06-26\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Powder Metallurgy\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://doi.org/10.1080/00325899.2023.2228093\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"METALLURGY & METALLURGICAL ENGINEERING\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Powder Metallurgy","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1080/00325899.2023.2228093","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"METALLURGY & METALLURGICAL ENGINEERING","Score":null,"Total":0}

引用次数: 0

摘要

本文章由计算机程序翻译，如有差异，请以英文原文为准。

查看原文本刊更多论文

Powder metallurgy processing of Nb-modified near β titanium alloys prepared with elemental powders

ABSTRACT Near β Ti alloys typically show high specific strength and provide a wide spectrum of mechanical properties with different heat treatments. In this work, a commercial near β Ti alloy Ti-5553 (Ti-5Al-5V-5Mo-3Cr-0.5Fe) was prepared through powder metallurgy using the blended elemental powder approach. Additionally, alloy modifications with 6 wt.% Nb (Ti-6Nb-5Al-2.5V-5Mo-3Cr-0.5Fe) and 12 wt.% Nb (Ti-12Nb-5Al-5Mo-3Cr-0.5Fe) were investigated. Specimens were prepared by uniaxial cold compaction of blended powders at room temperature with sintering conducted at 1300°C for 2 h under Ar atmosphere. Microstructure investigation revealed reasonable homogenisation of alloying elements and colony sizes in the order of 80-100 μm with porosity below 10%. Moreover, the bending strength of as-sintered Ti-12Nb-5Al-5Mo-3Cr-0.5Fe was about 850 MPa and the micro-Vickers hardness was approximately 370 HV. The alloy modifications with Nb increased strength without loss in flexural strain.

求助全文

通过发布文献求助，成功后即可免费获取论文全文。去求助

来源期刊

Powder Metallurgy 工程技术-冶金工程

CiteScore

2.90

自引率

7.10%

发文量

审稿时长

3 months

期刊介绍： Powder Metallurgy is an international journal publishing peer-reviewed original research on the science and practice of powder metallurgy and particulate technology. Coverage includes metallic particulate materials, PM tool materials, hard materials, composites, and novel powder based materials.