{"title":"基于渐进失效分析法确定和验证修补过的 T700SC/EC240A 复合材料层压板的修复公差","authors":"Z. R. Wu, Y. R. Yang, L. Hang","doi":"10.1007/s11029-024-10220-3","DOIUrl":null,"url":null,"abstract":"<p>The determination and verification of repair tolerance of patch-repaired laminates based on progressive failure analysis method was studied. The axial tensile tests of intact, perforated, and repaired specimens of T700SC/EC240A composite laminates were carried out. The damage process of composite laminates under tensile load was numerically simulated using the progressive damage degradation model of 3D Hashin–Ye failure criterion. A method for determining the repair tolerance of patch-repaired laminates was proposed, and the upper and lower limits of repair the composite laminates were derived. The result verified by the strength index of Boeing Company showed that the method for determining the repair tolerance proposed is reasonable and feasible.</p>","PeriodicalId":18308,"journal":{"name":"Mechanics of Composite Materials","volume":null,"pages":null},"PeriodicalIF":1.5000,"publicationDate":"2024-08-21","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Determination and Verification of Repair Tolerance of Patch Repaired T700SC/EC240A Composite Laminates Based on Progressive Failure Analysis Method\",\"authors\":\"Z. R. Wu, Y. R. Yang, L. Hang\",\"doi\":\"10.1007/s11029-024-10220-3\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p>The determination and verification of repair tolerance of patch-repaired laminates based on progressive failure analysis method was studied. The axial tensile tests of intact, perforated, and repaired specimens of T700SC/EC240A composite laminates were carried out. The damage process of composite laminates under tensile load was numerically simulated using the progressive damage degradation model of 3D Hashin–Ye failure criterion. A method for determining the repair tolerance of patch-repaired laminates was proposed, and the upper and lower limits of repair the composite laminates were derived. The result verified by the strength index of Boeing Company showed that the method for determining the repair tolerance proposed is reasonable and feasible.</p>\",\"PeriodicalId\":18308,\"journal\":{\"name\":\"Mechanics of Composite Materials\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":1.5000,\"publicationDate\":\"2024-08-21\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Mechanics of Composite Materials\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://doi.org/10.1007/s11029-024-10220-3\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q4\",\"JCRName\":\"MATERIALS SCIENCE, COMPOSITES\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Mechanics of Composite Materials","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1007/s11029-024-10220-3","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"MATERIALS SCIENCE, COMPOSITES","Score":null,"Total":0}

引用次数: 0

摘要

研究了基于渐进失效分析方法的修补修复层压板修复公差的确定和验证。对 T700SC/EC240A 复合材料层压板的完整试样、穿孔试样和修复试样进行了轴向拉伸试验。使用三维 Hashin-Ye 失效准则的渐进式损伤退化模型对复合材料层压板在拉伸载荷作用下的损伤过程进行了数值模拟。提出了确定修补修复层压板修复容限的方法，并得出了复合材料层压板的修复上下限。波音公司的强度指标验证结果表明，所提出的修复公差确定方法是合理可行的。

本文章由计算机程序翻译，如有差异，请以英文原文为准。

Determination and Verification of Repair Tolerance of Patch Repaired T700SC/EC240A Composite Laminates Based on Progressive Failure Analysis Method

查看原文本刊更多论文

Determination and Verification of Repair Tolerance of Patch Repaired T700SC/EC240A Composite Laminates Based on Progressive Failure Analysis Method

The determination and verification of repair tolerance of patch-repaired laminates based on progressive failure analysis method was studied. The axial tensile tests of intact, perforated, and repaired specimens of T700SC/EC240A composite laminates were carried out. The damage process of composite laminates under tensile load was numerically simulated using the progressive damage degradation model of 3D Hashin–Ye failure criterion. A method for determining the repair tolerance of patch-repaired laminates was proposed, and the upper and lower limits of repair the composite laminates were derived. The result verified by the strength index of Boeing Company showed that the method for determining the repair tolerance proposed is reasonable and feasible.

求助全文

通过发布文献求助，成功后即可免费获取论文全文。去求助

来源期刊

Mechanics of Composite Materials 工程技术-材料科学：复合

CiteScore

2.90

自引率

17.60%

发文量

审稿时长

12 months

期刊介绍： Mechanics of Composite Materials is a peer-reviewed international journal that encourages publication of original experimental and theoretical research on the mechanical properties of composite materials and their constituents including, but not limited to: damage, failure, fatigue, and long-term strength; methods of optimum design of materials and structures; prediction of long-term properties and aging problems; nondestructive testing; mechanical aspects of technology; mechanics of nanocomposites; mechanics of biocomposites; composites in aerospace and wind-power engineering; composites in civil engineering and infrastructure and other composites applications.