长期运行的钢制下水管道的腐蚀退化

IF 0.7 4区材料科学 Q4 MATERIALS SCIENCE, MULTIDISCIPLINARY

Materials Science Pub Date : 2024-06-18 DOI:10.1007/s11003-024-00808-4

V. D. Makarenko, O. V. Stogniy, V. I. Gots, S. Yu. Maksymov, Yu. V. Makarenko

{"title":"长期运行的钢制下水管道的腐蚀退化","authors":"V. D. Makarenko, O. V. Stogniy, V. I. Gots, S. Yu. Maksymov, Yu. V. Makarenko","doi":"10.1007/s11003-024-00808-4","DOIUrl":null,"url":null,"abstract":"<p>The results of the experimental study of the degradation of steel structures of sewer underground constructions are presented. The distribution of harmful gas elements (sulfur, hydrogen, oxygen) over the wall thickness of sewer pipes along corrosion defects in the form of pits, as well as the character of changes in the microhardness of the metal depending on the hydrogen content and service life, are shown. To confirm the metal softening with increasing hydrogen concentration, the stresses of the crystal lattice (distortion stresses) were measured.</p>","PeriodicalId":18230,"journal":{"name":"Materials Science","volume":"111 9 1","pages":""},"PeriodicalIF":0.7000,"publicationDate":"2024-06-18","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Corrosion Degradation of Long-Term Operated Steel Sewer Pipes\",\"authors\":\"V. D. Makarenko, O. V. Stogniy, V. I. Gots, S. Yu. Maksymov, Yu. V. Makarenko\",\"doi\":\"10.1007/s11003-024-00808-4\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p>The results of the experimental study of the degradation of steel structures of sewer underground constructions are presented. The distribution of harmful gas elements (sulfur, hydrogen, oxygen) over the wall thickness of sewer pipes along corrosion defects in the form of pits, as well as the character of changes in the microhardness of the metal depending on the hydrogen content and service life, are shown. To confirm the metal softening with increasing hydrogen concentration, the stresses of the crystal lattice (distortion stresses) were measured.</p>\",\"PeriodicalId\":18230,\"journal\":{\"name\":\"Materials Science\",\"volume\":\"111 9 1\",\"pages\":\"\"},\"PeriodicalIF\":0.7000,\"publicationDate\":\"2024-06-18\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Materials Science\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://doi.org/10.1007/s11003-024-00808-4\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q4\",\"JCRName\":\"MATERIALS SCIENCE, MULTIDISCIPLINARY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials Science","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1007/s11003-024-00808-4","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}

引用次数: 0

摘要

本文介绍了下水道地下建筑钢结构退化的实验研究结果。结果显示了有害气体元素（硫、氢、氧）在下水道管道壁厚上的分布，以及金属显微硬度随氢含量和使用寿命而变化的特征。为了证实金属随着氢浓度的增加而软化，测量了晶格的应力（畸变应力）。

本文章由计算机程序翻译，如有差异，请以英文原文为准。

Corrosion Degradation of Long-Term Operated Steel Sewer Pipes

查看原文本刊更多论文

Corrosion Degradation of Long-Term Operated Steel Sewer Pipes

The results of the experimental study of the degradation of steel structures of sewer underground constructions are presented. The distribution of harmful gas elements (sulfur, hydrogen, oxygen) over the wall thickness of sewer pipes along corrosion defects in the form of pits, as well as the character of changes in the microhardness of the metal depending on the hydrogen content and service life, are shown. To confirm the metal softening with increasing hydrogen concentration, the stresses of the crystal lattice (distortion stresses) were measured.

求助全文

通过发布文献求助，成功后即可免费获取论文全文。去求助

来源期刊

Materials Science 工程技术-材料科学：综合

CiteScore

1.60

自引率

44.40%

发文量

审稿时长

4-8 weeks

期刊介绍： Materials Science reports on current research into such problems as cracking, fatigue and fracture, especially in active environments as well as corrosion and anticorrosion protection of structural metallic and polymer materials, and the development of new materials.