Densification Behaviours of TiC/Ni Metal Ceramic Alloys Produced by Powder Metallurgy

Ceramic Metallic Alloys of TiC/Ni, Comprising Titanium Carbide with Nickel Contents of 5%, 15%, 30%, and 50%, were Fabricated through Solid-Phase Sintering at 1400°C with a 2-hour Holding Time and a Pressure of 50MPa. This Study Explores the Impact of Nickel Content on the Mechanical and Structural Properties. The Solidification Mechanism between TiC and Ni is Governed by Carbon Diffusion through TiC Particles, Affecting the Morphology of TiC and Carbon Particles in Ni Samples. The Reaction Behavior within the TiC/Ni Alloys was Analyzed, and Microstructural and Mechanical Characteristics were Examined to Evaluate the Influence of Varying Nickel Contents. Results indicate that in all samples, the TiC matrix exhibited a solid solution of the FCC phase. The reaction mechanism of Ti-C-Ni reveals the evolution of solid phase formation with increasing nickel content. As nickel content increases, the mass and size of nickel particles grow, leading to a more uniform and homogeneous structure. At a nickel content of 15%, the samples displayed a bending strength of 1200 ± 50 N, a microhardness of 800 ± 20 (HV 0.1), and a density of 5.6 ± 0.2.