Influence of tool geometry on mechanical and microstructural characteristics of friction stir welded cast alloys

Cast alloys find suitable applicability in aerospace sector owing to low porosity, high specific strength, corrosion resistance, fluidity and good machinability. The investigation focuses on friction stir welding (FSW) of cast A356 and A2014 alloys with varied range of process parameters, namely tool pin shape (cylinder, threaded cylinder, square, and conical), tool rotation speed (1800–2100 rpm) and welding speed (10–25 mm × min−1). Experimentation on stirwelding was performed based on selected tool pin shape between varied tool rotation and welding speed. The output responses, namely Ultimate tensile strength (UTS) and micro hardness, have been evaluated to study the effect of each tool. The microstructural characteristics of the weld samples were analyzed using optical microscope and scanning electron microscope (SEM) technique. The microstructural observation unveiled that complete fusion prevails between the parent alloys devoid of micro porosities and segregations. The re-crystallization effect resulted in the finer grains. The cylinder-shaped tool with a thread and square shaped tool rendered better strength and hardness properties of 136.6 MPa and 109.4 HV, respectively.