Influence of zinc-containing compounds on the properties of ceramic materials based on the Li2O–MgO–Al2O3–SiO2 system

The results of a study the influence of magnesium oxide substitution with zinc oxide in the Li2O–MgO– Al2O3–SiO2 system, as well as the introduction of pre-synthesized ganite ZnAl2O4, on sintering, phase formation and thermal expansion of synthesized materials are presented. It was found that after substitution of 4 % magnesium oxide MgO with zinc oxide ZnO, the ceramic material synthesized at a temperature of 1 150 °C was characterized by higher values of apparent density (not less than 1 835 kg/m3), mechanical compressive strength (300 MPa), and heat resistance (more than 80 thermal cycles), as well as low values of LTEC (–0,25 ∙ 10–6 K–1), which is due to the formation of crystalline phases of spodumene, spinel, forsterite, corundum, ganite and quartz.