通过反应性无针电纺丝制备多孔 Nb2O5 纳米纤维以应用于锂硫电池

IF 3.1 4区 化学 Q2 CHEMISTRY, INORGANIC & NUCLEAR
I. Shepa, E. Múdra, D. Capková, A. Kovalčíková, Ondrej Petrus, Frantisek Kromka, O. Milkovič, V. Antal, M. Baláž, M. Lisnichuk, Dominika Marcin-Behunova, D. Zalka, Ján Dusza
{"title":"通过反应性无针电纺丝制备多孔 Nb2O5 纳米纤维以应用于锂硫电池","authors":"I. Shepa, E. Múdra, D. Capková, A. Kovalčíková, Ondrej Petrus, Frantisek Kromka, O. Milkovič, V. Antal, M. Baláž, M. Lisnichuk, Dominika Marcin-Behunova, D. Zalka, Ján Dusza","doi":"10.3390/inorganics11120456","DOIUrl":null,"url":null,"abstract":"This contribution describes the preparation, coupled with detailed characterization, of Nb2O5 nanofibers and their application in lithium–sulfur batteries for the improvement of electrochemical performance. The utilization of reactive needle-less electrospinning allowed us to obtain, in a single step, amorphous pre-ceramic composite PAN/Nb2O5 fibers, which were transformed into porous ceramic Nb2O5 nanofibers via calcination. Thermogravimetric studies defined that calcination at 600 °C results in crystalline ceramic fibers without carbon residues. The fibrous morphology and mean diameter (614 ± 100 nm) of the ceramic nanofibers were analyzed via scanning and transmission electron microscopy. A surface area of 7.472 m2/g was determined through nitrogen adsorption measurements, while a combination of X-ray diffraction and Raman spectroscopy was used to show the crystallinity and composition of the fibers after calcination—single T-phase Nb2O5. Its performance in the cathode of lithium–sulfur batteries was defined through electrochemical tests, and the obtained results were compared to a similar blank electrode. The initial discharge capacity of 0.5 C reached a value of 570 mAh∙g−1, while the reversible capacity of 406 mAh∙g−1 was retained after 200 cycles, representing a capacity retention of 71.3%. The presence of Nb2O5 nanofibers in the carbon cathode inhibits the shuttle effect through polysulphide confinement, which originates from porosity and chemical trapping.","PeriodicalId":13572,"journal":{"name":"Inorganics","volume":"26 1","pages":""},"PeriodicalIF":3.1000,"publicationDate":"2023-11-25","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Porous Nb2O5 Nanofibers Prepared via Reactive Needle-Less Electrospinning for Application in Lithium–Sulfur Batteries\",\"authors\":\"I. Shepa, E. Múdra, D. Capková, A. Kovalčíková, Ondrej Petrus, Frantisek Kromka, O. Milkovič, V. Antal, M. Baláž, M. Lisnichuk, Dominika Marcin-Behunova, D. Zalka, Ján Dusza\",\"doi\":\"10.3390/inorganics11120456\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"This contribution describes the preparation, coupled with detailed characterization, of Nb2O5 nanofibers and their application in lithium–sulfur batteries for the improvement of electrochemical performance. The utilization of reactive needle-less electrospinning allowed us to obtain, in a single step, amorphous pre-ceramic composite PAN/Nb2O5 fibers, which were transformed into porous ceramic Nb2O5 nanofibers via calcination. Thermogravimetric studies defined that calcination at 600 °C results in crystalline ceramic fibers without carbon residues. The fibrous morphology and mean diameter (614 ± 100 nm) of the ceramic nanofibers were analyzed via scanning and transmission electron microscopy. A surface area of 7.472 m2/g was determined through nitrogen adsorption measurements, while a combination of X-ray diffraction and Raman spectroscopy was used to show the crystallinity and composition of the fibers after calcination—single T-phase Nb2O5. Its performance in the cathode of lithium–sulfur batteries was defined through electrochemical tests, and the obtained results were compared to a similar blank electrode. The initial discharge capacity of 0.5 C reached a value of 570 mAh∙g−1, while the reversible capacity of 406 mAh∙g−1 was retained after 200 cycles, representing a capacity retention of 71.3%. The presence of Nb2O5 nanofibers in the carbon cathode inhibits the shuttle effect through polysulphide confinement, which originates from porosity and chemical trapping.\",\"PeriodicalId\":13572,\"journal\":{\"name\":\"Inorganics\",\"volume\":\"26 1\",\"pages\":\"\"},\"PeriodicalIF\":3.1000,\"publicationDate\":\"2023-11-25\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Inorganics\",\"FirstCategoryId\":\"92\",\"ListUrlMain\":\"https://doi.org/10.3390/inorganics11120456\",\"RegionNum\":4,\"RegionCategory\":\"化学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"CHEMISTRY, INORGANIC & NUCLEAR\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Inorganics","FirstCategoryId":"92","ListUrlMain":"https://doi.org/10.3390/inorganics11120456","RegionNum":4,"RegionCategory":"化学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"CHEMISTRY, INORGANIC & NUCLEAR","Score":null,"Total":0}
引用次数: 0

摘要

这篇论文介绍了 Nb2O5 纳米纤维的制备及其详细表征,以及它们在锂硫电池中的应用,以改善电化学性能。利用无针反应电纺丝技术,我们只需一步就能获得无定形的预陶瓷复合 PAN/Nb2O5 纤维,并通过煅烧将其转化为多孔陶瓷 Nb2O5 纳米纤维。热重研究表明,在 600 °C 下煅烧可产生无碳残留的结晶陶瓷纤维。通过扫描和透射电子显微镜分析了陶瓷纳米纤维的纤维形态和平均直径(614 ± 100 nm)。通过氮吸附测量确定了 7.472 m2/g 的表面积,同时结合 X 射线衍射和拉曼光谱显示了煅烧后纤维的结晶度和成分--单 T 相 Nb2O5。通过电化学测试确定了其在锂硫电池阴极中的性能,并将所得结果与类似的空白电极进行了比较。0.5 C 的初始放电容量达到了 570 mAh∙g-1 的值,而经过 200 次循环后,可逆容量仍为 406 mAh∙g-1 ,容量保持率为 71.3%。碳阴极中 Nb2O5 纳米纤维的存在通过多硫化物的封闭抑制了穿梭效应,这种效应源于多孔性和化学捕获。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
Porous Nb2O5 Nanofibers Prepared via Reactive Needle-Less Electrospinning for Application in Lithium–Sulfur Batteries
This contribution describes the preparation, coupled with detailed characterization, of Nb2O5 nanofibers and their application in lithium–sulfur batteries for the improvement of electrochemical performance. The utilization of reactive needle-less electrospinning allowed us to obtain, in a single step, amorphous pre-ceramic composite PAN/Nb2O5 fibers, which were transformed into porous ceramic Nb2O5 nanofibers via calcination. Thermogravimetric studies defined that calcination at 600 °C results in crystalline ceramic fibers without carbon residues. The fibrous morphology and mean diameter (614 ± 100 nm) of the ceramic nanofibers were analyzed via scanning and transmission electron microscopy. A surface area of 7.472 m2/g was determined through nitrogen adsorption measurements, while a combination of X-ray diffraction and Raman spectroscopy was used to show the crystallinity and composition of the fibers after calcination—single T-phase Nb2O5. Its performance in the cathode of lithium–sulfur batteries was defined through electrochemical tests, and the obtained results were compared to a similar blank electrode. The initial discharge capacity of 0.5 C reached a value of 570 mAh∙g−1, while the reversible capacity of 406 mAh∙g−1 was retained after 200 cycles, representing a capacity retention of 71.3%. The presence of Nb2O5 nanofibers in the carbon cathode inhibits the shuttle effect through polysulphide confinement, which originates from porosity and chemical trapping.
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
Inorganics
Inorganics Chemistry-Inorganic Chemistry
CiteScore
2.80
自引率
10.30%
发文量
193
审稿时长
6 weeks
期刊介绍: Inorganics is an open access journal that covers all aspects of inorganic chemistry research. Topics include but are not limited to: synthesis and characterization of inorganic compounds, complexes and materials structure and bonding in inorganic molecular and solid state compounds spectroscopic, magnetic, physical and chemical properties of inorganic compounds chemical reactivity, physical properties and applications of inorganic compounds and materials mechanisms of inorganic reactions organometallic compounds inorganic cluster chemistry heterogenous and homogeneous catalytic reactions promoted by inorganic compounds thermodynamics and kinetics of significant new and known inorganic compounds supramolecular systems and coordination polymers bio-inorganic chemistry and applications of inorganic compounds in biological systems and medicine environmental and sustainable energy applications of inorganic compounds and materials MD
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
确定
请完成安全验证×
copy
已复制链接
快去分享给好友吧!
我知道了
右上角分享
点击右上角分享
0
联系我们:info@booksci.cn Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。 Copyright © 2023 布克学术 All rights reserved.
京ICP备2023020795号-1
ghs 京公网安备 11010802042870号
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术官方微信