Early hydration studies of cementitious materials incorporating nanoalumina

Concrete technologists use different types of additives such as fly ash, slag, natural pozzolans and nanomaterials toenhance concrete performance and durability. However, a detailed explanation of the early-age hydration process and microstructural modification of concrete in the presence of nanomaterials remains to be presented and extensive research is required for strategic modification of cementitious systems. This study focused on the precise monitoring of early-age hydration with the incorporation of nanoalumina (nAl) in tricalcium silicate (C₃S) and Portland cement paste and mortar. The dosage of nAl was varied from 1 to 5% (by weight) in C₃S and from 0.1 to 1.0% in Portland cement, with a water/cement ratio of 0.4. The hydration studies showed that the nAl increased the cross-linkage in calcium silicate hydrate gel through substitution of aluminium by silicon, which was responsible for the enhancement of the modulus of elasticity (by 40%) with 1.0% nAl) after 7 days of hydration. In summary, the incorporation of nAl modified the concrete microstructure in the initial days of hydration, leading to higher concrete performance and longer service lives of concrete structures.