Tribological Wear of as Cast Zn-4Al Alloy Cooled at Various Rates from the Eutectoid Transformation Temperature

The paper presents the results from a study on the impact of the cooling rate in the eutectoid transition on the abrasive wear of the as cast Zn-4Al alloy. The microstructure of the researched material consists of dendrites of the η solid solution and an ( α+η ) eutectic structure. During the eutectoid transformation at 275 o C the distribution in the eutectic structure was transformed and fined. Heat treatment was carried out for this alloy, during which three cooling mediums were used, i.e. water, air and an furnace. For the research material obtained in this way, metallographic examinations were performed using the methods of light and scanning electron microscopy, as well as hardness measurements. It was found that faster cooling rate promoted the fragmentation of structural components, which translates into higher hardness of the material. This also had effects in the tribological wear of the tested alloy. As part of the tests, an abrasive wear test was carried out on a standard T-07 tester