The micro-capacitance enhancement of polyionic liquids grafted onto carbon nanotubes on the piezoelectric properties of poly(vinylidene fluoride) films and their sensor applications

ABSTRACTThe increased micro-capacitance of a poly (vinylidene fluoride) (PVDF) matrix can effectively improve the piezoelectric properties of the composite material. This work used chemically modified carbon nanotubes (CNTs) as the main reinforcement material. Atom transfer radical polymerization (ATRP) was used to graft polyionic liquids (PILs) with different hydrophilic anions to the CNTs’ surfaces. Solution casting and compressive melt molding were used to prepare the PVDF-composite piezoelectric films. Micro-capacitance formed by the PIL grafted CNTs dispersed well in the PVDF matrix, and their effects on the crystalline form and piezoelectric properties were studied. The hydrophobic hexafluorophosphate anion (-PF6-) can significantly improve the CNTs dispersion and enhance the micro-capacitance formation in the PVDF matrix. During solution crystallization, the synergistic effect of CNTs and PIL on the PVDF and the solvent effect made the content of β phase of PVDF/CNTs@PIL-PF6 film reach 80.2%, resulting in a high dielectric constant of 188 and a piezoelectric coefficient of 36. In the process of melt crystallization, due to shear stretching and extrusion, the CNTs@PIL-PF6 had an obvious nucleation effect on the polar crystalline phase of PVDF, with a β phase content up to 99.3%, leading to the higher dielectric constant of 530 and the piezoelectric coefficient of 31. The current discovery provides a development direction for smart piezoelectric polymer matrix composites, which have great potential in preparing piezoelectric energy storage materials.KEYWORDS: poly(vinylidene fluoride)carbon nanotubespolyionic liquidpiezoelectricitydielectric propertiespolar phaseDisclaimerAs a service to authors and researchers we are providing this version of an accepted manuscript (AM). Copyediting, typesetting, and review of the resulting proofs will be undertaken on this manuscript before final publication of the Version of Record (VoR). During production and pre-press, errors may be discovered which could affect the content, and all legal disclaimers that apply to the journal relate to these versions also. AcknowledgmentThis research was supported by the National Natural Science Foundation of China (21406017), Changzhou Science and Technology Support Plan (Social Development)(CZ20230022), the Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD), the Top-notch Academic Programs Project of Jiangsu Higher Education Institutions (TAPP). The Postgraduate Research & Practice Innovation Program of Jiangsu Province (KYCX23_3045) is also acknowledged.