{"title":"[牙用磷酸锌水泥的疲劳]。","authors":"K Okazaki, F Nishimura","doi":"","DOIUrl":null,"url":null,"abstract":"<p><p>The fatigue characteristics of a zinc phosphate cement were examined. Using a split mould made of stainless steel, 12 mm x phi 6 mm column shape specimens were prepared. Fatigue tests were done by loading partially repeated pulsating diametrical tensile stress of 1-20 Hz, minimum stress was 0.2 MPa (2.0 kgf/cm2) and maximum stress was 3.5-5.4 MPa (36-55 kgf/cm2). During testing, the specimen was kept under distilled water. The existence of a fatigue was confirmed and there were marked signs of fatigue on the fracture surface. The relation between maximum stress and the number of cycles to fracture (S-N diagram) was obtained. Therefore the following equation and fatigue parameter (n) were deduced. logS + 0.0775.logN = 0.8931 n = 12.9 The fatigue characteristics depended on the frequency, that is, a time to fracture was shorter at the loading frequency of 20 Hz than that of 1 Hz.</p>","PeriodicalId":77622,"journal":{"name":"Shika zairyo, kikai = Journal of the Japanese Society for Dental Materials and Devices","volume":"9 6","pages":"871-7"},"PeriodicalIF":0.0000,"publicationDate":"1990-11-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"[Fatigue of dental zinc phosphate cement].\",\"authors\":\"K Okazaki, F Nishimura\",\"doi\":\"\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p><p>The fatigue characteristics of a zinc phosphate cement were examined. Using a split mould made of stainless steel, 12 mm x phi 6 mm column shape specimens were prepared. Fatigue tests were done by loading partially repeated pulsating diametrical tensile stress of 1-20 Hz, minimum stress was 0.2 MPa (2.0 kgf/cm2) and maximum stress was 3.5-5.4 MPa (36-55 kgf/cm2). During testing, the specimen was kept under distilled water. The existence of a fatigue was confirmed and there were marked signs of fatigue on the fracture surface. The relation between maximum stress and the number of cycles to fracture (S-N diagram) was obtained. Therefore the following equation and fatigue parameter (n) were deduced. logS + 0.0775.logN = 0.8931 n = 12.9 The fatigue characteristics depended on the frequency, that is, a time to fracture was shorter at the loading frequency of 20 Hz than that of 1 Hz.</p>\",\"PeriodicalId\":77622,\"journal\":{\"name\":\"Shika zairyo, kikai = Journal of the Japanese Society for Dental Materials and Devices\",\"volume\":\"9 6\",\"pages\":\"871-7\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"1990-11-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Shika zairyo, kikai = Journal of the Japanese Society for Dental Materials and Devices\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Shika zairyo, kikai = Journal of the Japanese Society for Dental Materials and Devices","FirstCategoryId":"1085","ListUrlMain":"","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
The fatigue characteristics of a zinc phosphate cement were examined. Using a split mould made of stainless steel, 12 mm x phi 6 mm column shape specimens were prepared. Fatigue tests were done by loading partially repeated pulsating diametrical tensile stress of 1-20 Hz, minimum stress was 0.2 MPa (2.0 kgf/cm2) and maximum stress was 3.5-5.4 MPa (36-55 kgf/cm2). During testing, the specimen was kept under distilled water. The existence of a fatigue was confirmed and there were marked signs of fatigue on the fracture surface. The relation between maximum stress and the number of cycles to fracture (S-N diagram) was obtained. Therefore the following equation and fatigue parameter (n) were deduced. logS + 0.0775.logN = 0.8931 n = 12.9 The fatigue characteristics depended on the frequency, that is, a time to fracture was shorter at the loading frequency of 20 Hz than that of 1 Hz.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号