{"title":"热处理对板条马氏体的影响","authors":"E. R. Fábián, Áron Kótai","doi":"10.2478/amt-2018-0008","DOIUrl":null,"url":null,"abstract":"Abstract During our investigation lath martensite was produced in low carbon steels by austenitization at 1200 °C/20 min, and the cooling of samples in ice water. The samples were tempered at a range of temperatures. The tempering effects on microstructure and on mechanical proprieties were investigated. Some samples with lath martensite microstructure were cold rolled and heat treated at different temperatures. Recrystallization was observed after heat treatment at 600-700 °C.","PeriodicalId":426392,"journal":{"name":"Acta Materialia Transilvanica","volume":"8 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2018-04-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"1","resultStr":"{\"title\":\"Heat Treatment Effect on Lath Martensite\",\"authors\":\"E. R. Fábián, Áron Kótai\",\"doi\":\"10.2478/amt-2018-0008\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Abstract During our investigation lath martensite was produced in low carbon steels by austenitization at 1200 °C/20 min, and the cooling of samples in ice water. The samples were tempered at a range of temperatures. The tempering effects on microstructure and on mechanical proprieties were investigated. Some samples with lath martensite microstructure were cold rolled and heat treated at different temperatures. Recrystallization was observed after heat treatment at 600-700 °C.\",\"PeriodicalId\":426392,\"journal\":{\"name\":\"Acta Materialia Transilvanica\",\"volume\":\"8 1\",\"pages\":\"0\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2018-04-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"1\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Acta Materialia Transilvanica\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.2478/amt-2018-0008\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Acta Materialia Transilvanica","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.2478/amt-2018-0008","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Abstract During our investigation lath martensite was produced in low carbon steels by austenitization at 1200 °C/20 min, and the cooling of samples in ice water. The samples were tempered at a range of temperatures. The tempering effects on microstructure and on mechanical proprieties were investigated. Some samples with lath martensite microstructure were cold rolled and heat treated at different temperatures. Recrystallization was observed after heat treatment at 600-700 °C.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号