{"title":"稻壳灰和纤维素工业渣部分替代水泥对混凝土抗压强度的影响","authors":"","doi":"10.33922/j.ujet_v5i1_1","DOIUrl":null,"url":null,"abstract":"In this research work, the effect of rice husk ash on concrete produced with cellulose industrial residue was studied. A mix proportion of 1:1.8:3.7 with water cement ratio of 0.47 were used. The percentage replacement of Ordinary Portland Cement (OPC) with cellulose industrial residue and rice husk ash used were 0%, 5%, 10%, 20% 30% and 40%. Concrete cubes of 150mm x 150mm x 150mm of Ordinary Portland Cement/Cellulose Industrial Residue and Ordinary Portland Cement/Cellulose Industrial Residue/Rice Ash were cast and cured at 3,7,28,60 and 90 days respectively. At the end of each hydration period, the concrete cubes were crushed and their compressive strength were determined. The result of compressive strength of 5-40% replacement of cement with cellulose industrial residue ranges from 13.02-32.81 N/mm2 as against 25.60-42.08N/mm2 for the control test. The result of the compressive strength of 5-40% replacement of cement with Cellulose Industrial Residue and Rice Husk Ash ranges from 13.17-36.30N/mm2 as against 25.60-42.08N/mm2 for the control test. The result of the initial and final setting time of Ordinary Portland Cement/Cellulose Industrial Residue and Cement/Cellulose Industrial Residue/Rice Husk Ash for 5-40% replacement of cement ranges from 61-118mins, 58-110mins and 620 – 836mins, 598 – 799mins respectively as against 52mins and 590mins for the control test. The main conclusion of this study is that the incorporation rice husk ash into cellulose industrial residue increase the strength of concrete produced. The objective of this study is to assess the strength of concrete produced when two pozzolanic materials were used to replace cement in producing concrete.","PeriodicalId":151670,"journal":{"name":"UMUDIKE JOURNAL OF ENGINEERING AND TECHNOLOGY","volume":"49 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"1900-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"EFFECT OF PARTIAL REPLACEMENT OF CEMENT WITH RICE HUSK ASH AND CELLULOSE INDUSTRIAL RESIDUE ON COMPRESSIVE STRENGTH OF CONCRETE\",\"authors\":\"\",\"doi\":\"10.33922/j.ujet_v5i1_1\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"In this research work, the effect of rice husk ash on concrete produced with cellulose industrial residue was studied. A mix proportion of 1:1.8:3.7 with water cement ratio of 0.47 were used. The percentage replacement of Ordinary Portland Cement (OPC) with cellulose industrial residue and rice husk ash used were 0%, 5%, 10%, 20% 30% and 40%. Concrete cubes of 150mm x 150mm x 150mm of Ordinary Portland Cement/Cellulose Industrial Residue and Ordinary Portland Cement/Cellulose Industrial Residue/Rice Ash were cast and cured at 3,7,28,60 and 90 days respectively. At the end of each hydration period, the concrete cubes were crushed and their compressive strength were determined. The result of compressive strength of 5-40% replacement of cement with cellulose industrial residue ranges from 13.02-32.81 N/mm2 as against 25.60-42.08N/mm2 for the control test. The result of the compressive strength of 5-40% replacement of cement with Cellulose Industrial Residue and Rice Husk Ash ranges from 13.17-36.30N/mm2 as against 25.60-42.08N/mm2 for the control test. The result of the initial and final setting time of Ordinary Portland Cement/Cellulose Industrial Residue and Cement/Cellulose Industrial Residue/Rice Husk Ash for 5-40% replacement of cement ranges from 61-118mins, 58-110mins and 620 – 836mins, 598 – 799mins respectively as against 52mins and 590mins for the control test. The main conclusion of this study is that the incorporation rice husk ash into cellulose industrial residue increase the strength of concrete produced. The objective of this study is to assess the strength of concrete produced when two pozzolanic materials were used to replace cement in producing concrete.\",\"PeriodicalId\":151670,\"journal\":{\"name\":\"UMUDIKE JOURNAL OF ENGINEERING AND TECHNOLOGY\",\"volume\":\"49 1\",\"pages\":\"0\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"1900-01-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"UMUDIKE JOURNAL OF ENGINEERING AND TECHNOLOGY\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.33922/j.ujet_v5i1_1\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"UMUDIKE JOURNAL OF ENGINEERING AND TECHNOLOGY","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.33922/j.ujet_v5i1_1","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
EFFECT OF PARTIAL REPLACEMENT OF CEMENT WITH RICE HUSK ASH AND CELLULOSE INDUSTRIAL RESIDUE ON COMPRESSIVE STRENGTH OF CONCRETE
In this research work, the effect of rice husk ash on concrete produced with cellulose industrial residue was studied. A mix proportion of 1:1.8:3.7 with water cement ratio of 0.47 were used. The percentage replacement of Ordinary Portland Cement (OPC) with cellulose industrial residue and rice husk ash used were 0%, 5%, 10%, 20% 30% and 40%. Concrete cubes of 150mm x 150mm x 150mm of Ordinary Portland Cement/Cellulose Industrial Residue and Ordinary Portland Cement/Cellulose Industrial Residue/Rice Ash were cast and cured at 3,7,28,60 and 90 days respectively. At the end of each hydration period, the concrete cubes were crushed and their compressive strength were determined. The result of compressive strength of 5-40% replacement of cement with cellulose industrial residue ranges from 13.02-32.81 N/mm2 as against 25.60-42.08N/mm2 for the control test. The result of the compressive strength of 5-40% replacement of cement with Cellulose Industrial Residue and Rice Husk Ash ranges from 13.17-36.30N/mm2 as against 25.60-42.08N/mm2 for the control test. The result of the initial and final setting time of Ordinary Portland Cement/Cellulose Industrial Residue and Cement/Cellulose Industrial Residue/Rice Husk Ash for 5-40% replacement of cement ranges from 61-118mins, 58-110mins and 620 – 836mins, 598 – 799mins respectively as against 52mins and 590mins for the control test. The main conclusion of this study is that the incorporation rice husk ash into cellulose industrial residue increase the strength of concrete produced. The objective of this study is to assess the strength of concrete produced when two pozzolanic materials were used to replace cement in producing concrete.