热处理对1570、1580和1590铝合金力学性能的影响

E. V. Aryshensky, V. Aryshensky, A. Drits, F. Grechnikov, A. A. Ragazin
{"title":"热处理对1570、1580和1590铝合金力学性能的影响","authors":"E. V. Aryshensky, V. Aryshensky, A. Drits, F. Grechnikov, A. A. Ragazin","doi":"10.18287/2541-7533-2022-21-4-76-87","DOIUrl":null,"url":null,"abstract":"The study addresses the effect of thermal treatment on the mechanical properties and grain size of magnesium rich alloys with small scandium additions 1570, 1580 and 1590. The effect of preheat temperature (within 260440 С range) and soaking time (within 2 100 hours range) on yield strength, tensile strength and relative elongation of the alloys under investigation was analyzed. Mechanical properties were determined using uniaxial tensile tests in accordance with ISO 6892-1. In addition, for some modes the microstructure was studied for Al3Mg2 -phase presence and distribution by optical metallography methods depending on thermal treatment conditions. The studies demonstrated that supersaturated solid solution in the 1570 alloy decomposes faster in the entire studied temperature range, and after 48 hours soaking, its strength properties start degrading. At the same time, the 1580 and 1590 alloys are much more thermally stable, with slightly lower yield strength after long soaking time, while tensile strength remains unchanged. The conditions of 260 C annealing temperature are not favorable for plastic properties, severely degrading (due to -phase formation) in the 1570 and 1580 alloys. Plastic properties degradation is not so evident at higher soaking temperature, however, the 1590 alloy maintains the highest plasticity indices.","PeriodicalId":265584,"journal":{"name":"VESTNIK of Samara University. Aerospace and Mechanical Engineering","volume":"42 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2023-01-18","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Thermal treatment effect on the mechanical properties of 1570, 1580 and 1590 aluminum alloys\",\"authors\":\"E. V. Aryshensky, V. Aryshensky, A. Drits, F. Grechnikov, A. A. Ragazin\",\"doi\":\"10.18287/2541-7533-2022-21-4-76-87\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The study addresses the effect of thermal treatment on the mechanical properties and grain size of magnesium rich alloys with small scandium additions 1570, 1580 and 1590. The effect of preheat temperature (within 260440 С range) and soaking time (within 2 100 hours range) on yield strength, tensile strength and relative elongation of the alloys under investigation was analyzed. Mechanical properties were determined using uniaxial tensile tests in accordance with ISO 6892-1. In addition, for some modes the microstructure was studied for Al3Mg2 -phase presence and distribution by optical metallography methods depending on thermal treatment conditions. The studies demonstrated that supersaturated solid solution in the 1570 alloy decomposes faster in the entire studied temperature range, and after 48 hours soaking, its strength properties start degrading. At the same time, the 1580 and 1590 alloys are much more thermally stable, with slightly lower yield strength after long soaking time, while tensile strength remains unchanged. The conditions of 260 C annealing temperature are not favorable for plastic properties, severely degrading (due to -phase formation) in the 1570 and 1580 alloys. Plastic properties degradation is not so evident at higher soaking temperature, however, the 1590 alloy maintains the highest plasticity indices.\",\"PeriodicalId\":265584,\"journal\":{\"name\":\"VESTNIK of Samara University. Aerospace and Mechanical Engineering\",\"volume\":\"42 1\",\"pages\":\"0\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2023-01-18\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"VESTNIK of Samara University. Aerospace and Mechanical Engineering\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.18287/2541-7533-2022-21-4-76-87\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"VESTNIK of Samara University. Aerospace and Mechanical Engineering","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.18287/2541-7533-2022-21-4-76-87","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0

摘要

研究了热处理对1570、1580和1590三种微量钪富镁合金力学性能和晶粒尺寸的影响。分析了预热温度(260440 С范围内)和保温时间(2100 h范围内)对合金屈服强度、抗拉强度和相对延伸率的影响。机械性能根据ISO 6892-1采用单轴拉伸试验测定。此外,利用光学金相方法研究了不同热处理条件下某些模式下Al3Mg2相的存在和分布。研究表明,1570合金中过饱和固溶体在整个温度范围内分解速度较快,浸泡48 h后,其强度性能开始退化。同时,1580和1590合金的热稳定性好得多,长时间浸泡后屈服强度略有下降,而抗拉强度保持不变。260℃的退火温度对1570和1580合金的塑性性能不利,严重退化(由于-相的形成)。在较高的浸泡温度下,1590合金的塑性性能下降不明显,但塑性指标保持最高。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
Thermal treatment effect on the mechanical properties of 1570, 1580 and 1590 aluminum alloys
The study addresses the effect of thermal treatment on the mechanical properties and grain size of magnesium rich alloys with small scandium additions 1570, 1580 and 1590. The effect of preheat temperature (within 260440 С range) and soaking time (within 2 100 hours range) on yield strength, tensile strength and relative elongation of the alloys under investigation was analyzed. Mechanical properties were determined using uniaxial tensile tests in accordance with ISO 6892-1. In addition, for some modes the microstructure was studied for Al3Mg2 -phase presence and distribution by optical metallography methods depending on thermal treatment conditions. The studies demonstrated that supersaturated solid solution in the 1570 alloy decomposes faster in the entire studied temperature range, and after 48 hours soaking, its strength properties start degrading. At the same time, the 1580 and 1590 alloys are much more thermally stable, with slightly lower yield strength after long soaking time, while tensile strength remains unchanged. The conditions of 260 C annealing temperature are not favorable for plastic properties, severely degrading (due to -phase formation) in the 1570 and 1580 alloys. Plastic properties degradation is not so evident at higher soaking temperature, however, the 1590 alloy maintains the highest plasticity indices.
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
自引率
0.00%
发文量
0
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
确定
请完成安全验证×
copy
已复制链接
快去分享给好友吧!
我知道了
右上角分享
点击右上角分享
0
联系我们:info@booksci.cn Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。 Copyright © 2023 布克学术 All rights reserved.
京ICP备2023020795号-1
ghs 京公网安备 11010802042870号
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术官方微信