{"title":"醋酸盐纳米纤维素的生产和分类方法与电旋法","authors":"M. Harahap, L. Zai","doi":"10.51544/kimia.v6i1.2978","DOIUrl":null,"url":null,"abstract":"In this research, cellulose acetate fiber was produced by electrospinning method. Cellulose acetate was dissolved with acetone solvent and then putin to a cooling system torestrain the rate of evaporation of cellulose acetate. The conductivity and evaporation rate of the cellulose acetate solution were tested, and the cellulose acetate fiber sproduced were tested using scanning electron microscopy (SEM). The conductivity of the cellulose acetate solutionwas 3.45 S/cm at 15oC and almost doubled at 22oC. The cooling system test was ableto maintain the temperature of the cellulose acetate solution at 15 oC for approximately 2 minutes. In addition, bead fibers are produced due to their low conductivity.","PeriodicalId":332205,"journal":{"name":"JURNAL KIMIA SAINTEK DAN PENDIDIKAN","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2022-07-24","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"PRODUKSI DAN KARAKTERISASI NANOSERAT SELULOSA ASETAT DENGAN METODE ELEKTROSPINING\",\"authors\":\"M. Harahap, L. Zai\",\"doi\":\"10.51544/kimia.v6i1.2978\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"In this research, cellulose acetate fiber was produced by electrospinning method. Cellulose acetate was dissolved with acetone solvent and then putin to a cooling system torestrain the rate of evaporation of cellulose acetate. The conductivity and evaporation rate of the cellulose acetate solution were tested, and the cellulose acetate fiber sproduced were tested using scanning electron microscopy (SEM). The conductivity of the cellulose acetate solutionwas 3.45 S/cm at 15oC and almost doubled at 22oC. The cooling system test was ableto maintain the temperature of the cellulose acetate solution at 15 oC for approximately 2 minutes. In addition, bead fibers are produced due to their low conductivity.\",\"PeriodicalId\":332205,\"journal\":{\"name\":\"JURNAL KIMIA SAINTEK DAN PENDIDIKAN\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2022-07-24\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"JURNAL KIMIA SAINTEK DAN PENDIDIKAN\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.51544/kimia.v6i1.2978\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"JURNAL KIMIA SAINTEK DAN PENDIDIKAN","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.51544/kimia.v6i1.2978","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
PRODUKSI DAN KARAKTERISASI NANOSERAT SELULOSA ASETAT DENGAN METODE ELEKTROSPINING
In this research, cellulose acetate fiber was produced by electrospinning method. Cellulose acetate was dissolved with acetone solvent and then putin to a cooling system torestrain the rate of evaporation of cellulose acetate. The conductivity and evaporation rate of the cellulose acetate solution were tested, and the cellulose acetate fiber sproduced were tested using scanning electron microscopy (SEM). The conductivity of the cellulose acetate solutionwas 3.45 S/cm at 15oC and almost doubled at 22oC. The cooling system test was ableto maintain the temperature of the cellulose acetate solution at 15 oC for approximately 2 minutes. In addition, bead fibers are produced due to their low conductivity.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号