Effect of Production Conditions of Wood Powder on Bending Properties of Wood Powder Molding Material without Adhesive

The effect of production conditions of wood powder on the bending properties of wood powder molding material was investigated. Wood powder was produced by milling wood into powder under conditions of different temperatures (25◦C, 100◦C) and moisture contents (0%MC, about 30%MC). Molding materials were produced from wood powder in stream atmosphere of high temperature and high pressure (175◦C, 900 kPa) using self-bonding ability of the wood powder. Adhesives, such as a synthetic resin, were not used. To evaluate the bending properties of the molding materials, the modulus of elasticity and the bending strength were examined by static three-point bending test. As for the characteristic of wood particle, in case of wood particle produced by milling wood under a condition of high temperature and high moisture content (100◦C and about 30%MC), tendencies for intercellular layer to be exposed on surface of a particle and for the aspect ratio of particles to be large were confirmed. And in that case, the molding material showed the highest value in modulus of elasticity and bending strength. It is highly probable that the inprovement of the self-bonding ability of wood powder and the increase of the aspect ratio of wood particle take part in the improvement of strength properties of molding material.