Composition-dependent sign inversion of the Soret coefficient of SiO2 in binary borosilicate melts.

Using a laser-induced local-heating experiment combined with temperature analysis, we observed the composition-dependent sign inversion of the Soret coefficient of SiO2 in binary silicate melts, which was successfully explained by a modified Kempers model used for describing the Soret effect in oxide melts. In particular, the diffusion of SiO2 to the cold side under a temperature gradient, which is an anomaly in silicate melts, was observed in the SiO2-poor compositions. The theoretical model indicates that the thermodynamic mixing properties of oxides, partial molar enthalpy of mixing, and partial molar volume are the dominant factors for determining the migration direction of the SiO2 component under a temperature gradient.