{"title":"镍基合金焚烧炉内衬失效","authors":"","doi":"10.31399/asm.fach.usage.c0091756","DOIUrl":null,"url":null,"abstract":"\n An alloy IN-690 (N06690) incinerator liner approximately 0.8 mm (0.031 in.) thick failed after only 250 h of service burning solid waste. Investigation supported the conclusion that the root cause of the failure was overfiring during startup and sulfidation of the nickel-base alloy. No recommendations were made.","PeriodicalId":194756,"journal":{"name":"ASM Failure Analysis Case Histories: Improper Maintenance, Repair, and Operating Conditions","volume":"19 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2019-06-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Failure of a Nickel-Base Alloy Incinerator Liner\",\"authors\":\"\",\"doi\":\"10.31399/asm.fach.usage.c0091756\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"\\n An alloy IN-690 (N06690) incinerator liner approximately 0.8 mm (0.031 in.) thick failed after only 250 h of service burning solid waste. Investigation supported the conclusion that the root cause of the failure was overfiring during startup and sulfidation of the nickel-base alloy. No recommendations were made.\",\"PeriodicalId\":194756,\"journal\":{\"name\":\"ASM Failure Analysis Case Histories: Improper Maintenance, Repair, and Operating Conditions\",\"volume\":\"19 1\",\"pages\":\"0\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2019-06-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"ASM Failure Analysis Case Histories: Improper Maintenance, Repair, and Operating Conditions\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.31399/asm.fach.usage.c0091756\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"ASM Failure Analysis Case Histories: Improper Maintenance, Repair, and Operating Conditions","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.31399/asm.fach.usage.c0091756","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}

引用次数: 0

摘要

合金in -690 (N06690)焚烧炉衬里约0.8毫米(0.031英寸)厚，在燃烧固体废物仅250小时后就失效了。调查结果表明，失效的根本原因是镍基合金在启动过程中的过烧和硫化。没有提出任何建议。

本文章由计算机程序翻译，如有差异，请以英文原文为准。

查看原文本刊更多论文

Failure of a Nickel-Base Alloy Incinerator Liner

An alloy IN-690 (N06690) incinerator liner approximately 0.8 mm (0.031 in.) thick failed after only 250 h of service burning solid waste. Investigation supported the conclusion that the root cause of the failure was overfiring during startup and sulfidation of the nickel-base alloy. No recommendations were made.

求助全文

通过发布文献求助，成功后即可免费获取论文全文。去求助

来源期刊

ASM Failure Analysis Case Histories: Improper Maintenance, Repair, and Operating Conditions

自引率

0.00%

发文量