Magnetic and Mössbauer Studies of Some Mixed Cobaltites of the Lanthanides and Alkali Metals

Magnetic and Mossbauer studies are carried out on compounds Mx, Ln1−x, CoO3 where M is Ba or Sr and Ln is La, Nd or Dy. All compositions with x > 0.2 with the exception of the dysprosium compounds are ferromagnetic at low temperatures. From hysteresis and initial susceptibility studies, it is concluded that they contain a number of single domain clusters in a paramagnetic matrix. Mossbauer spectra of Ba0.3Nd0.7CoO3 and Ba0.5Dy0.5CoO3 show two resonance lines and that of Sr0.5La0.5CoO3 shows a single line spectrum at all temperatures, and no hyperfine spectra are shown even far below TC. The results are interpreted in terms of short-range magnetic ordering in these systems. An MxLn1−x, CoO3,-Verbindungen, wobei M = Ba oder Sr und Ln = La, Nd oder Dy bedeuten, werden magnetische und Mosbaueruntersuchungen durchgefuhrt. Alle Zusammensetzungen mit × > 0,2 mit Ausnahme der Dysprosiumverbindungen sind ferromagnetisch bei tiefen Tempera-turen. Aus den Untersuchungen der Hysteresis und der Anfangssuszeptibilitat wird geschlossen, dar sie eine Anzahl von Ein-Domanenklustern in einer paramagnetischen Matrix enthalten. Die Mosbauerspektren von Ba0,3Nd0,7CoO3 und Ba0,5Dy0,5O3, zeigen zwei Resonanzlinien und die von Sr0,5La0,5CoO3 bei allen Temperaturen ein Ein-Linienspektrum und bis weit unterhalb Tc werden keine Hyperfeinspektren beobachtet. Die Ergebnisse werden rnit magnetischer Nahordnung in diesen Systemen interpretiert.