Effect of sodium/calcium hypochlorite on adhesion and adaptation of fiber posts luted with a dual resin cement.

Abstract

This study aimed to evaluate the effect of different concentrations of sodium hypochlorite (NaOCl) and calcium hypochlorite [Ca(OCl)2] on the bond strength and adaptation of glass fiber posts luted with a dual-curing resin cement. Fifty decoronated premolars were sectioned 14 mm from the apex and endodontically treated. The root canal filling was partially removed. The specimens were divided into 5 groups (n=10) according to the irrigant for post space irrigation: 0.9% sodium chloride (NaCl), (control); 2.5% NaOCl; 5.25% NaOCl; 2.5% Ca(OCl)2; and 5.25% Ca(OCl)2. For each group, irrigation was performed with 5 ml of solution. Afterward, the posts were luted with a dual-curing resin cement. One slice from each third was obtained and submitted to the push-out test and failure modes analysis. An additional slice from the middle third was submitted to confocal images for analysis of adaptation failures (gaps). Two-way ANOVA, Tukey's post-hoc, Kruskal-Wallis with Bonferroni adjusted, and chi-square tests, analyzed data. The group treated with 5.25% NaOCl showed lower bond strength values and generated more cohesive failures compared to the control (p < 0.05). Bond strength decreased from coronal to apical in the post space (p < 0.001). The groups treated with NaOCl had the highest percentages of gaps compared to the control (p < 0.05). Regardless of concentration, Ca(OCl)2 did not influence the bond strength and the occurrence of gaps (P > 0.05). Ca(OCl)2 is a good option for irrigating the post space before luting a fiber post with a dual-curing resin cement.