Surface Corrosion of Mg-Containing Al-Based Alloys

Abstract

During heat-treatment of Mg-containing Al-based alloys, the Mg concentration changes considerably. As compared to the pure material significant surface corrosion is observed for the air heattreated alloy. In vacuum heat treatment the Mg content of the surface layer increases considerably. Initially metallic Mg is detected on the surface which, however, becomes oxidized later on. On the basis of the investigations one has to assume that the process is not a simple diffusion mechanism only. A new conception is formed for the process according to which it is controlled by the breaking up of the Al2O3 barrier layer by Mg. Wahrend einer Warmebehandlung von Mg enthaltenden Al-Legierungen andert sich die Mg-Konzentration betrachtlich. Im Vergleich zu dem reinen Material wird eine signifikante Oberflachenkorrosion fur in Luft getemperte Legierungen beobachtet. Bei Vakuumtemperung steigt der Mg-Gehalt der Oberflachenschicht betrachtlich an. Anfangs wird metallisches Mg auf der Oberflache nachgewiesen, das jedoch spater oxidiert wird. Auf der Grundlage der Untersuchungen mus angenommen werden, das der Prozess nicht nur ein einfacher Diffusionsmechanismus ist. Eine neue Vorstellung fur den Prozes wird vorgeschlagen, derzufolge dieser Prozes durch das Aufbrechen der Al2O3-Barrierenschicht durch Mg gesteuert wird.