Wear Behaviors of WC-CoCr and WC-CrC-Ni Coatings Sprayed by HVOF

Abstract

The high-velocity oxy-fuel (HVOF) thermal spraying coating technique has been considered a promising replacement for traditional electrolytic hard chrome plating (EHC), which caused environmental pollution and lung cancer due to toxic Cr. In this paper, two types of cermet coatings were prepared by HVOF spraying: WC-CoCr and WC-CrC-Ni coatings. The produced coatings were analyzed extensively in terms of the micro-hardness, porosity, crystalline phase and microstructure using a hardness tester, optical microscopy, X-ray diffraction, and scanning electron microscopy (including energy dispersed spectroscopy (EDS)), respectively. The wear and friction behaviors of the coatings were evaluated comparatively by reciprocating sliding wear tests at 25 °C, 250 °C, and 450 °C. The results revealed correlations among the microstructures, metallic binder matrixes, porosities, and wear performance of the coatings. For example, WC-CoCr coatings showed better sliding wear resistance than WC-CrC-Ni coatings, regardless of the test temperature due to the more homogeneous microstructure, Co-rich, Cr-rich metallic binder matrix, and lower porosity. 요 약 경질 크롬 도금은 도금과정에서 유독성 물질인 Cr을 배출시키기 때문에 환경오염과 폐암을 유발하고 있어 최근 고속화염 용사법 (HVOF)을 이용한 코팅 방법이 대체 방법으로 각광받고 있다. 본 연구에서는 HVOF 방법을 이용 하여 경질 크롬 도금 방법을 대체하기 위한 WC-CoCr과 WC-CrC-Ni 서멧 코팅을 제조하였으며, 제조된 코팅층의 물 리적/화학적 특성인 미세경도, 기공도, 결정상 및 미세구조를 경도기, 광학현미경, X-선 회절 (XRD), 주사전자현미경 (SEM) 및 EDS를 이용하여 분석하였다. 코팅층의 마모 및 마찰 거동 분석을 위해 왕복 슬라이딩 마모 테스트 방법을 이용하여 25 °C, 250 °C, 450 °C의 온도에서 실시하였으며, 두 코팅층의 마모/마찰 특성을 비교 평가하여, 코팅층의 내마모 성능이 미세구조와 금속기지 결합제 간의 연관성이 있음을 확인하였다. 결과적으로 미세구조가 균일하고, 기공도 가 낮을수록 내마모성이 향상되고, 금속기지 결합제가 많을수록 우수한 내마모성을 나타내는 것으로 확인되었다. 즉, 균 일한 미세구조와 과량의 Co, Cr 금속기지 결합제, 낮은 기공도로 인해 온도와 테스트 온도와 관계없이 WC-CoCr 코팅 이 WC-CrC-Ni 코팅에 비해 내마모성이 우수한 것으로 나타났다.