Optimal slag content for geopolymer composites under freeze-thaw cycles with different freezing temperatures

IF 3.3 3区 工程技术 Q1 ENGINEERING, MULTIDISCIPLINARY
L. Fan, Weiliang Zhong, Guang Wang, Y. Xi
{"title":"Optimal slag content for geopolymer composites under freeze-thaw cycles with different freezing temperatures","authors":"L. Fan, Weiliang Zhong, Guang Wang, Y. Xi","doi":"10.1631/jzus.A2200437","DOIUrl":null,"url":null,"abstract":"Improving the freeze-thaw resistance of geopolymers is of great significance to ensure their durability in cold regions. This study presents an experimental investigation of optimal slag content for geopolymer composites under freeze-thaw cycles with different freezing temperatures. Firstly, five kinds of geopolymer composites with 10.0%, 20.0%, 30.0%, 40.0%, and 50.0% slag contents and 1.0% fiber content were prepared. Freeze-thaw cycle tests at −1.0 ℃, −20.0 ℃, and −40.0 ℃ were carried out for these geopolymer composites and their physical and mechanical properties after the freeze-thaw cycle were tested. The results show that the porosity of the geopolymer composites decreases as the slag content increases. Their mass loss ratio and strength loss ratio increase gradually as the freezing temperature decreases. The mass loss ratio and strength loss ratio of geopolymer composites after freeze-thaw cycles all decrease as the slag content increases. Considering the physical and mechanical properties of geopolymers after freeze-thaw cycles, the optimal slag contents are 40.0% and 50.0%. 目的 提高地聚物的抗冻融循环性能对确保地聚物在寒区中的耐久性具有重要意义。本文旨在研究冻结温度对矿渣改性的偏高岭土基地聚物物理和力学性能的影响,以期为地聚物在寒区中的实际应用和耐久性评估提供参考。 创新点 提出了冻融循环条件下地聚物复合材料的最佳矿渣含量;2. 发现矿渣的掺入可以抑制地聚物在寒冷环境中的开裂,提高地聚物复合材料的抗冻融性。 方法 制备不同矿渣的纤维增强聚合物并对其开展三种冻结温度的冻融循环试验;2. 分析不同矿渣的纤维增强聚合物的孔隙结构特性;3. 分析冻融循环后不同矿渣的纤维增强聚合物的物理力学性能;4. 提出冻融循环作用下地聚物复合材料的最佳矿渣含量。 结论 随着矿渣含量的增加,地聚物复合材料的孔隙率降低,且凝胶孔和过渡孔均逐渐减小;2. 冻融循环后,地聚物复合材料中的裂缝宽度和数量都随着矿渣含量的增加而减少,表明矿渣的掺入可以抑制地聚物在寒冷环境中的开裂;3. 矿渣的掺入可以显著降低地聚物复合材料在冻融循环后的质量损失率和强度损失率,进而提高地聚物复合材料的抗冻融性;4. 40.0%和50.0%矿渣含量的地聚物复合材料在冻融循环后仍能保持较高的力学性能。","PeriodicalId":17508,"journal":{"name":"Journal of Zhejiang University-SCIENCE A","volume":"16 1","pages":"366-376"},"PeriodicalIF":3.3000,"publicationDate":"2023-04-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Zhejiang University-SCIENCE A","FirstCategoryId":"5","ListUrlMain":"https://doi.org/10.1631/jzus.A2200437","RegionNum":3,"RegionCategory":"工程技术","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"ENGINEERING, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 0

Abstract

Improving the freeze-thaw resistance of geopolymers is of great significance to ensure their durability in cold regions. This study presents an experimental investigation of optimal slag content for geopolymer composites under freeze-thaw cycles with different freezing temperatures. Firstly, five kinds of geopolymer composites with 10.0%, 20.0%, 30.0%, 40.0%, and 50.0% slag contents and 1.0% fiber content were prepared. Freeze-thaw cycle tests at −1.0 ℃, −20.0 ℃, and −40.0 ℃ were carried out for these geopolymer composites and their physical and mechanical properties after the freeze-thaw cycle were tested. The results show that the porosity of the geopolymer composites decreases as the slag content increases. Their mass loss ratio and strength loss ratio increase gradually as the freezing temperature decreases. The mass loss ratio and strength loss ratio of geopolymer composites after freeze-thaw cycles all decrease as the slag content increases. Considering the physical and mechanical properties of geopolymers after freeze-thaw cycles, the optimal slag contents are 40.0% and 50.0%. 目的 提高地聚物的抗冻融循环性能对确保地聚物在寒区中的耐久性具有重要意义。本文旨在研究冻结温度对矿渣改性的偏高岭土基地聚物物理和力学性能的影响,以期为地聚物在寒区中的实际应用和耐久性评估提供参考。 创新点 提出了冻融循环条件下地聚物复合材料的最佳矿渣含量;2. 发现矿渣的掺入可以抑制地聚物在寒冷环境中的开裂,提高地聚物复合材料的抗冻融性。 方法 制备不同矿渣的纤维增强聚合物并对其开展三种冻结温度的冻融循环试验;2. 分析不同矿渣的纤维增强聚合物的孔隙结构特性;3. 分析冻融循环后不同矿渣的纤维增强聚合物的物理力学性能;4. 提出冻融循环作用下地聚物复合材料的最佳矿渣含量。 结论 随着矿渣含量的增加,地聚物复合材料的孔隙率降低,且凝胶孔和过渡孔均逐渐减小;2. 冻融循环后,地聚物复合材料中的裂缝宽度和数量都随着矿渣含量的增加而减少,表明矿渣的掺入可以抑制地聚物在寒冷环境中的开裂;3. 矿渣的掺入可以显著降低地聚物复合材料在冻融循环后的质量损失率和强度损失率,进而提高地聚物复合材料的抗冻融性;4. 40.0%和50.0%矿渣含量的地聚物复合材料在冻融循环后仍能保持较高的力学性能。
不同冻结温度下地聚合物复合材料的最佳含渣量
提高地聚合物的抗冻融性能对保证其在寒冷地区的耐久性具有重要意义。本文对不同冻结温度下地聚合物复合材料的最佳含渣量进行了试验研究。首先制备了矿渣含量分别为10.0%、20.0%、30.0%、40.0%、50.0%和纤维含量分别为1.0%的5种地聚合物复合材料。分别在- 1.0℃、- 20.0℃和- 40.0℃进行了冻融循环试验,测试了冻融循环后地聚合物复合材料的物理力学性能。结果表明:随着渣含量的增加,地聚合物复合材料的孔隙率降低;随着冻结温度的降低,其质量损失率和强度损失率逐渐增大。冻融循环后地聚合物复合材料的质量损失率和强度损失率均随渣含量的增加而减小。考虑冻融循环后地聚合物的物理力学性能,最佳矿渣掺量为40.0%和50.0%。目的 提高地聚物的抗冻融循环性能对确保地聚物在寒区中的耐久性具有重要意义。本文旨在研究冻结温度对矿渣改性的偏高岭土基地聚物物理和力学性能的影响,以期为地聚物在寒区中的实际应用和耐久性评估提供参考。 创新点 提出了冻融循环条件下地聚物复合材料的最佳矿渣含量;2. 发现矿渣的掺入可以抑制地聚物在寒冷环境中的开裂,提高地聚物复合材料的抗冻融性。 方法 制备不同矿渣的纤维增强聚合物并对其开展三种冻结温度的冻融循环试验;2. 分析不同矿渣的纤维增强聚合物的孔隙结构特性;3. 分析冻融循环后不同矿渣的纤维增强聚合物的物理力学性能;4. 提出冻融循环作用下地聚物复合材料的最佳矿渣含量。 结论 随着矿渣含量的增加,地聚物复合材料的孔隙率降低,且凝胶孔和过渡孔均逐渐减小;2. 冻融循环后,地聚物复合材料中的裂缝宽度和数量都随着矿渣含量的增加而减少,表明矿渣的掺入可以抑制地聚物在寒冷环境中的开裂;3. 矿渣的掺入可以显著降低地聚物复合材料在冻融循环后的质量损失率和强度损失率,进而提高地聚物复合材料的抗冻融性;4. 40.0%, 50.0%。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 求助全文
来源期刊
Journal of Zhejiang University-SCIENCE A
Journal of Zhejiang University-SCIENCE A 工程技术-工程:综合
CiteScore
5.60
自引率
12.50%
发文量
2964
审稿时长
2.9 months
期刊介绍: Journal of Zhejiang University SCIENCE A covers research in Applied Physics, Mechanical and Civil Engineering, Environmental Science and Energy, Materials Science and Chemical Engineering, etc.
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
确定
请完成安全验证×
copy
已复制链接
快去分享给好友吧!
我知道了
右上角分享
点击右上角分享
0
联系我们:info@booksci.cn Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。 Copyright © 2023 布克学术 All rights reserved.
京ICP备2023020795号-1
ghs 京公网安备 11010802042870号
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术官方微信