Identifying the Effect of PWHT on Strength of Laser Beam Welding Joints of AA2024 Aluminum Alloy

Abstract

The corrosion-resistant and strength-to-weight ratios are the primary factors in high-strength aluminum alloy. Hence, the AA2024 alloy is a possible candidate in the critical structural fabrication industry. The traditional joining method is ineffective for welding aluminum alloys. Higher melting point and temperature variations cause alloy isolation; porosity and hot cracking are caused by melting point variations. As a result, to fabricate joints, a light heat source laser beam was used. The weaker area of most fusion-welded joints was the heat-affected zone (HAZ). The post-weld heat treatment was used at HAZ to improve the properties. According to the experimental findings, the joint welded with solution treatment and artificial aging had a maximum tensile strength of 358 MPa. Re-precipitation of precipitates may accomplish in HAZ.