{"title":"Antistatic modification of polyester with carboxyterminated poly(oxyethylene)","authors":"Yaoming Zhao, Junwu Chen, Y. Sano, Y. Kimura","doi":"10.1002/APMC.1994.052170113","DOIUrl":null,"url":null,"abstract":"Carboxy-terminated poly(oxyethylenes) (PEO-acid) with number-average molecular weights Mn = 8400, 3300, and 1000 were used for antielectrostatic modification of poly(ethylene terephthalate) (PET). The blend PET fibers containing 2.0 and 5.0 wt.-% of PEO-acids were melt-spun at 285°C with an ordinary extruder and then drawn about 4.5-fold at 80°C. The processabilities of spinning and drawing were excellent at higher molecular weights of PEO-acid. The anti-electrostatic properties of the blend fibers became also improved with increasing molecular weight of PEO-acid. Since little ester interchange reaction took place between PET and PEO-acid during meltspinning, the blend fibers could retain almost the same mechanical properties as the original PET fiber. \n \n \n \nCarboxy-terminierte Polyoxyethylene (PEO-acid) mit zahlenmittleren Molekulargewichten Mn = 8400, 3300 und 1000 wurden zur antielektrostatischen Modifizierung von Polyethylenterephthalat (PET) verwendet. Fasern aus PET-PEO-acid-Blends mit 2,0 oder 5,0 Gew.-% PEO-acid wurden bei 285°C mit einem normalen Extruder aus der Schmelze gesponnen und anschliesend bei 80°C um das ca. 4,5fache verstreckt. Die Verarbeitbarkeit beim Verspinnen und Verstrecken war bei Verwendung von PEO-acid mit hohen Molekulargewichten ausgezeichnet. Die anti-elektrostatischen Eigenschaften wurden ebenfalls mit steigendem PEO-acid-Molekulargewicht besser. Da eine Umesterung beim Verspinnen nur in geringem Ausmas stattfand, blieben die mechanischen Eigenschaften der Blend-Fasern gegenuber den PET-Fasern nahezu unverandert.","PeriodicalId":7808,"journal":{"name":"Angewandte Makromolekulare Chemie","volume":"68 1","pages":"129-137"},"PeriodicalIF":0.0000,"publicationDate":"1994-04-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"4","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Angewandte Makromolekulare Chemie","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1002/APMC.1994.052170113","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 4
Abstract
Carboxy-terminated poly(oxyethylenes) (PEO-acid) with number-average molecular weights Mn = 8400, 3300, and 1000 were used for antielectrostatic modification of poly(ethylene terephthalate) (PET). The blend PET fibers containing 2.0 and 5.0 wt.-% of PEO-acids were melt-spun at 285°C with an ordinary extruder and then drawn about 4.5-fold at 80°C. The processabilities of spinning and drawing were excellent at higher molecular weights of PEO-acid. The anti-electrostatic properties of the blend fibers became also improved with increasing molecular weight of PEO-acid. Since little ester interchange reaction took place between PET and PEO-acid during meltspinning, the blend fibers could retain almost the same mechanical properties as the original PET fiber.
Carboxy-terminierte Polyoxyethylene (PEO-acid) mit zahlenmittleren Molekulargewichten Mn = 8400, 3300 und 1000 wurden zur antielektrostatischen Modifizierung von Polyethylenterephthalat (PET) verwendet. Fasern aus PET-PEO-acid-Blends mit 2,0 oder 5,0 Gew.-% PEO-acid wurden bei 285°C mit einem normalen Extruder aus der Schmelze gesponnen und anschliesend bei 80°C um das ca. 4,5fache verstreckt. Die Verarbeitbarkeit beim Verspinnen und Verstrecken war bei Verwendung von PEO-acid mit hohen Molekulargewichten ausgezeichnet. Die anti-elektrostatischen Eigenschaften wurden ebenfalls mit steigendem PEO-acid-Molekulargewicht besser. Da eine Umesterung beim Verspinnen nur in geringem Ausmas stattfand, blieben die mechanischen Eigenschaften der Blend-Fasern gegenuber den PET-Fasern nahezu unverandert.