Mechanism of Nanostructured Fluorapatite Formation from CaO, CaF2 and P2O5 Precursors by Mechanochemical Synthesis

Abstract

We determined the mechanism of mechanochemical synthesis of fluorapatite from CaO, CaF2 and P2O5 by characterisation of the intermediate compounds. We used atomic absorption spectroscopy, X-ray diffraction, field emission scanning electron microscopy, FTIR spectroscopy and transmission electron microscopy to find the transitional compounds. Investigation of the binary and ternary powder mixtures revealed the appearance of H3PO4, Ca(OH)2, Ca2P2O7 and CaCO3 as the intermediate compounds. At early stages of the milling, conversions of P2O5 to H3PO4 and CaO to Ca(OH)2 occurred in the wet atmosphere. Later, a combination of Ca(OH)2 and H3PO4 formed C a2P2O7 while the unreacted CaO was converted to CaCO3 by CO2 of the ambient atmosphere. Spherical crystalline Ca10 (PO4)6F2 particles formed after 48 hours of milling due to the reaction between Ca2P2O7, CaCO3 and CaF2.