Uji Kinerja Sistem Elektrokoagulasi terhadap Kobalt, Nikel, dan Mangan

Jurnal Sains Teknologi Lingkungan Pub Date : 2023-01-31 DOI:10.55981/jtl.2023.243

Oman Sulaeman, Karina Anggraeni, Muhammad Haqqiyuddin Robbani, Taty Hernaningsih

{"title":"Uji Kinerja Sistem Elektrokoagulasi terhadap Kobalt, Nikel, dan Mangan","authors":"Oman Sulaeman, Karina Anggraeni, Muhammad Haqqiyuddin Robbani, Taty Hernaningsih","doi":"10.55981/jtl.2023.243","DOIUrl":null,"url":null,"abstract":"The increasing demand for batteries for battery-based electric vehicles has caused the battery industry to grow rapidly. Batteries generally contain the heavy metals lithium, nickel, cobalt, and manganese. In solving the problem of battery’s heavy metal waste, wastewater treatment technologies is needed. One of the technologies that can be used is electrocoagulation technology. In this research, the performance test of electrocoagulation technology for the treatment of artificial wastewater containing cobalt, nickel, and manganese has been carried out. To determine the removal efficiency of the electrocoagulation system, 50 samples were collected from the processed products from each unit in the system. The results of the performance test of the electrocoagulation system showed that there was an effect of current on the pH value of artificial wastewater which increased by 11.43, 9.59, and 10.67% at currents of 10, 40, and 70 A; time affects the removal of cobalt, nickel and manganese with removal efficiencies reaching 93, 93, and 79%; and current has an effect on the removal of cobalt, nickel, and manganese in the electrocoagulation system as seen in the efficiency of removal of cobalt reaching 79, 90, and 95%; nickel removal efficiency reached 73, 85, and 97% while manganese removal efficiency was 76, 81, and 91% respectively at the same current of 10, 40, and 70 A.\n \nABSTRAK\nPeningkatan kebutuhan baterai untuk kendaraan listrik yang berbasis baterai menyebabkan industri baterai berkembang pesat. Baterai umumnya mengandung logam berat lithium, nikel, kobalt, dan mangan. Dalam memecahkan masalah limbah logam berat baterai ini diperlukan teknologi pengolahan air limbah. Salah satu teknologi yang bisa digunakan adalah dengan teknologi elektrokoagulasi. Dalam penelitian ini telah dilaksanakan uji kinerja perangkat teknologi elektrokoagulasi untuk pengolahan air limbah artifisial yang mengandung kobalt, nikel, dan mangan. Untuk mengetahui efisiensi penyisihan sistem elektrokoagulasi maka dilakukan pengumpulan 50 sampel dari hasil olahan dari masing-masing unit dalam sistem tersebut. Hasil uji kinerja sistem elektrokoagulasi menunjukkan adanya pengaruh arus terhadap nilai pH air limbah artifisial dimana mengalami kenaikan sebesar 11,43, 9,59, dan 10,67% pada arus 10, 40, dan 70 A; waktu berpengaruh terhadap proses penyisihan logam kobalt, nikel, dan mangan dengan efisiensi penyisihan mencapai 93%, 93% dan 79%; dan arus berpengaruh terhadap penyisihan kobalt, nikel, dan mangan pada sistem elektrokoagulasi yang terlihat pada efisiensi penyisihan kobalt mencapai 79, 90, dan 95%; efisiensi penyisihan nikel mencapai 73, 85, dan 97% sedangkan efisiensi penyisihan mangan sebesar 76, 81,dan 91% masing-masing pada arus yang sama 10, 40, dan 70 A.\n \n ","PeriodicalId":31853,"journal":{"name":"Jurnal Sains Teknologi Lingkungan","volume":"3 1","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2023-01-31","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Jurnal Sains Teknologi Lingkungan","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.55981/jtl.2023.243","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}

引用次数: 0

Abstract

The increasing demand for batteries for battery-based electric vehicles has caused the battery industry to grow rapidly. Batteries generally contain the heavy metals lithium, nickel, cobalt, and manganese. In solving the problem of battery’s heavy metal waste, wastewater treatment technologies is needed. One of the technologies that can be used is electrocoagulation technology. In this research, the performance test of electrocoagulation technology for the treatment of artificial wastewater containing cobalt, nickel, and manganese has been carried out. To determine the removal efficiency of the electrocoagulation system, 50 samples were collected from the processed products from each unit in the system. The results of the performance test of the electrocoagulation system showed that there was an effect of current on the pH value of artificial wastewater which increased by 11.43, 9.59, and 10.67% at currents of 10, 40, and 70 A; time affects the removal of cobalt, nickel and manganese with removal efficiencies reaching 93, 93, and 79%; and current has an effect on the removal of cobalt, nickel, and manganese in the electrocoagulation system as seen in the efficiency of removal of cobalt reaching 79, 90, and 95%; nickel removal efficiency reached 73, 85, and 97% while manganese removal efficiency was 76, 81, and 91% respectively at the same current of 10, 40, and 70 A. ABSTRAK Peningkatan kebutuhan baterai untuk kendaraan listrik yang berbasis baterai menyebabkan industri baterai berkembang pesat. Baterai umumnya mengandung logam berat lithium, nikel, kobalt, dan mangan. Dalam memecahkan masalah limbah logam berat baterai ini diperlukan teknologi pengolahan air limbah. Salah satu teknologi yang bisa digunakan adalah dengan teknologi elektrokoagulasi. Dalam penelitian ini telah dilaksanakan uji kinerja perangkat teknologi elektrokoagulasi untuk pengolahan air limbah artifisial yang mengandung kobalt, nikel, dan mangan. Untuk mengetahui efisiensi penyisihan sistem elektrokoagulasi maka dilakukan pengumpulan 50 sampel dari hasil olahan dari masing-masing unit dalam sistem tersebut. Hasil uji kinerja sistem elektrokoagulasi menunjukkan adanya pengaruh arus terhadap nilai pH air limbah artifisial dimana mengalami kenaikan sebesar 11,43, 9,59, dan 10,67% pada arus 10, 40, dan 70 A; waktu berpengaruh terhadap proses penyisihan logam kobalt, nikel, dan mangan dengan efisiensi penyisihan mencapai 93%, 93% dan 79%; dan arus berpengaruh terhadap penyisihan kobalt, nikel, dan mangan pada sistem elektrokoagulasi yang terlihat pada efisiensi penyisihan kobalt mencapai 79, 90, dan 95%; efisiensi penyisihan nikel mencapai 73, 85, dan 97% sedangkan efisiensi penyisihan mangan sebesar 76, 81,dan 91% masing-masing pada arus yang sama 10, 40, dan 70 A.

查看原文本刊更多论文

钴、镍和锰的电凝系统性能测试

基于电池的电动汽车对电池的需求不断增加，导致电池行业迅速增长。电池通常含有重金属锂、镍、钴和锰。在解决电池重金属废物问题时，需要废水处理技术。其中一种可用的技术是电凝技术。本研究对电絮凝技术处理含钴、镍、锰人工废水进行了性能试验。为了确定电混凝系统的去除效率，从系统中每个单元的处理产物中收集了50个样品。电絮凝系统性能测试结果表明，在10、40和70 A电流下，电流对人工废水pH值的影响分别提高了11.43%、9.59%和10.67%;时间影响钴、镍和锰的去除率，去除率分别达到93%、93%和79%;电流对电混凝系统中钴、镍和锰的去除有影响，钴的去除率分别达到79%、90%和95%;在10、40和70 A电流下，镍的去除率分别为73%、85%和97%，锰的去除率分别为76%、81%和91%。[摘要]peningkatan kebutuhan baterai untuk kendaraan listrik yang基础baterai产业baterai产业baterai产业。锂、镍、钴、锰。Dalam memecahkan masalah limbah logam berat baterai ini diperlukan技术，pengolahan空气limbah。Salah satu technologi yang bisa digunakan adalah dengan technologi elektrokoagulasi。Dalam penelitian ini telah dilaksanakan uji kinerja perangkat技术elektrokoagulasi untuk pengolahan空气limbah人工杨孟雄钴，镍，丹锰。Untuk mengetahui efisiensi penyisihan系统elektrokoagulasi maka dilakukan pengumpulan 50个样品dari hasil olahan dari - masing-masing单元dalam系统tersebut。Hasil uji kinerja系统elektrokoagulasi menunjukkan adanya pengaruh arus terhadap nilai pH air limbah人工dimana mengalami kenaikan sebesar 11,43, 9,59, dan10,67% paada arus 10, 40, dan70 A;Waktu berpengaruh terhadap工艺penyisihan logam kobalt，镍，danmangan dengan efisiensi penyisihan menapai 93%， 93% dan 79%;Dan arus berpengaruh terhadap penyisihan kobalt，镍，Dan mangan paada系统elektrokoagulasi Yang terlihat paada efisiensi penyisihan kobalt menapai 79,90, Dan 95%;镍镍合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金合金