Y. S. Soebianto, F. Yoshii, K. Makuuchi, I. Ishigaki
{"title":"Synthesis of hydrophilic elastomers by radiation grafting","authors":"Y. S. Soebianto, F. Yoshii, K. Makuuchi, I. Ishigaki","doi":"10.1002/APMC.1987.051520113","DOIUrl":null,"url":null,"abstract":"Radiation grafting of acrylic acid (AAc) onto ethylene-propylene rubber (EPR) to obtain hydrophilic elastomers has been investigated. It was found that by addition of alcohol (methanol and 1-propanol) into water as solvent for grafting the degree of grafting increased and formation of homopolymer was retarded. The grafting by addition of alcohol occurred even in deeper portions of the film compared with no addition of alcohol. Grafting rate differed largely with propylene contents in the EPR. Graft polymerization occurred easily in EPR of lower propylene contents such as 22%. Before introducing AAc in grafting the stability of EPR radicals of lower propylene contents was higher in comparison with other components. Water absorption of EPR increased linearly with increasing grafting yield. \n \n \n \nDie strahleninduzierte Pfropfung von Acrylsaure auf Ethylen-Propylen-Kautschuk (EPR) wurde untersucht. Es wurde gefunden, das die Pfropfungsgrade bei Zugabe von Alkohol (Methanol und Isopropanol) abnahmen und die Bildung der Homopolymeren verzogert wurde. Bei Zugabe von Alkohol fand Pfropfung auch im Innern des Filmes statt. Die Pfropfungsgeschwindigkeit war sehr stark vom Propylengehalt im EPR abhangig. Die Pfropfungspolymerisation fand bei kleinen Propylengehalten, z. B. bei 22%, leichter statt. Die Stabilitat der Radikale mit niedrigeren Propylengehalten war hoher als die der anderen. Die Wasseraufnahme der gepfropften Filme stiegen linear mit dem Pfropfungsgrad an.","PeriodicalId":7808,"journal":{"name":"Angewandte Makromolekulare Chemie","volume":"60 1","pages":"149-158"},"PeriodicalIF":0.0000,"publicationDate":"1987-07-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"10","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Angewandte Makromolekulare Chemie","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1002/APMC.1987.051520113","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 10
Abstract
Radiation grafting of acrylic acid (AAc) onto ethylene-propylene rubber (EPR) to obtain hydrophilic elastomers has been investigated. It was found that by addition of alcohol (methanol and 1-propanol) into water as solvent for grafting the degree of grafting increased and formation of homopolymer was retarded. The grafting by addition of alcohol occurred even in deeper portions of the film compared with no addition of alcohol. Grafting rate differed largely with propylene contents in the EPR. Graft polymerization occurred easily in EPR of lower propylene contents such as 22%. Before introducing AAc in grafting the stability of EPR radicals of lower propylene contents was higher in comparison with other components. Water absorption of EPR increased linearly with increasing grafting yield.
Die strahleninduzierte Pfropfung von Acrylsaure auf Ethylen-Propylen-Kautschuk (EPR) wurde untersucht. Es wurde gefunden, das die Pfropfungsgrade bei Zugabe von Alkohol (Methanol und Isopropanol) abnahmen und die Bildung der Homopolymeren verzogert wurde. Bei Zugabe von Alkohol fand Pfropfung auch im Innern des Filmes statt. Die Pfropfungsgeschwindigkeit war sehr stark vom Propylengehalt im EPR abhangig. Die Pfropfungspolymerisation fand bei kleinen Propylengehalten, z. B. bei 22%, leichter statt. Die Stabilitat der Radikale mit niedrigeren Propylengehalten war hoher als die der anderen. Die Wasseraufnahme der gepfropften Filme stiegen linear mit dem Pfropfungsgrad an.
研究了丙烯酸(AAc)与乙烯-丙烯橡胶(EPR)的辐射接枝制备亲水性弹性体。结果表明,在水中加入醇(甲醇和1-丙醇)作为接枝溶剂,接枝度提高,均聚物的形成减慢。与不添加醇相比,添加醇的接枝反应甚至发生在膜的较深部分。接枝率随EPR中丙烯含量的不同而有较大差异。在丙烯含量较低(22%)的EPR中容易发生接枝聚合。在引入AAc接枝前,丙烯含量较低的EPR自由基的稳定性高于其他组分。EPR的吸水率随接枝率的增加而线性增加。乙烯-丙烯- kautschuk (EPR)材料的制备。在此基础上,研究了乙醇和异丙醇(甲醇和异丙醇)的制备和均聚物的制备。《酒与酒》,《酒与酒》,《酒与酒》。pfropfungsgeswindigkeit war sehr stark from Propylengehalt in EPR hanging。模具前真菌的聚合和贝氏kleinenpropylengehalten, z.贝氏22%,leichter statt。Die stabilititder Radikale mit niedrigeren Propylengehalten war hoher也Die der anderen。[2] [1] [1] [1] [1] [1] [1] [1] [3]